Abstract:With the growth of the new energy industry, the requirements for manganese have increased significantly. In this paper, the method of manganese extraction from pyrolusite using ammonium sulfate roasting and water leaching was presented. At the optimal process parameters: mass ratio of (NH4)2SO4 to pyrolusite of 2:1, the roasting temperature of 420 degrees,C and duration of 120 min, the leaching efficiency of Mn and Fe was 94.55% and 54.38%, respectively. The mechanism analysis shows that MnO2 and Fe2O3 in pyrolusite were converted to (NH4)2Mn2(SO4)3, (NH4)3Fe(SO4)3, and NH4Fe(SO4)2 by roasting with ammonium sulfate. Iron was removed from the leaching solution with the addition of ammonia. Afterward, manganese carbonate products were prepared from iron-free manganese sulfate solution by adding ammonium carbonate at a stirring duration of 60 min, a reaction temperature of 40 degrees C, a pH of 7, and a molar ratio of ammonium carbonate to the manganese of 1.1:1, the precipitation efficiency of manganese could reach 99.8%, and the obtained manganese carbonate products were compliant with the industry standards. The ammonia released during the roasting process could be absorbed to regenerate (NH4)2SO4 and the final filtrate after evaporation and crystallization could be used to recycle (NH4)2SO4, both of which were used again into roasting process to reduce the consumption of raw material. In this process, the roasting temperature was only 420 degrees C, which was significantly lower than the pyrometallurgical process suggested in earlier studies.

Novel Process For Utilizing Low-Grade Manganese Oxide Ores By Sulfur-Based Reduction Roasting-Acid Leaching

Manganese Extraction by Sulfur-Based Reduction Roasting–acid Leaching from Low-Grade Manganese Oxide Ores

Researches on Techincal Conditions for Sulfur Reduction Roasting of Low-grade Manganese Oxide Ores

Extraction of Manganese from Iron Rich Mno2 Ores Via Selective Sulfation Roasting with So2 Followed by Water Leaching

Novel Process of Reduction Roasting Manganese Ore with Sulfur Waste and Extraction of Mn by Acid Leaching

Reduction of Low-Grade Manganese Oxide Ore by Biomass Roasting

A Process for Extraction of Manganese from Manganese Oxide Ores by a Novel and Efficient Roasting-Acid Leaching Technique

Efficient Extraction of Manganese from Low-Grade Pyrolusite by a Sawdust Pyrolysis Reduction Roasting-Acid Leaching Process

The Mechanism on Reducing Manganese Oxide Ore with Elemental Sulfur

Manganese extraction from high-iron-content manganese oxide ores by selective reduction roasting-acid leaching process using black charcoal as reductant

An Environmentally Friendly Approach for the Extraction and Recovery of Mn from Pyrolusite by Ammonium Sulfate Roasting‐water Leaching and Ammonium Carbonate Precipitation

Reductive Roasting of Iron-Rich Manganese Oxide Ore with Elemental Sulfur for Selective Manganese Extraction

Recovery of Manganese by Roasting-Ammonia Leaching from Low-Grade Manganese Carbonate Ores

Researches On Reduction Roasting Of Low-Grade Manganese Oxide Ores Using Biomass Charcoal As Reductant

Study in Reduction-Roast Leaching Manganese from Low-Grade Manganese Dioxide Ores Using Cornstalk As Reductant

Novel Understanding of Simultaneous Extraction of Vanadium and Manganese from Vanadium Slag and Low-Grade Pyrolusite Based on Selective Oxidation–Reduction Roasting

Green and Efficient Utilization of Ferruginous Gibbsite Ore and Ferruginous Manganese Ore by Synergetic Carbothermic Co-Reduction–Magnetic Separation Process

Characterization Of Sulfidation Roasting Of An Iron-Rich Manganese Oxide Ore With Elemental Sulfur

Mechanism of Reduction Roasting Manganese Oxide Using Pyriteunder Anaerobic Conditions

Extraction of Various Valuable Elements from Oceanic Manganese Nodules using Coal Gasification Slag via Reduction Roasting-Acid Leaching Process

An Innovative Technology for Full Component Recovery of Iron and Manganese from Low Grade Iron-Bearing Manganese Ore