Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Investigations into the Surface Strain/Stress State in a Single-Crystal Superalloy Via XRD Characterization

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Effects of Crystal Orientation and External Stress on the Static Recrystallization Behavior of an Ni-Based Single-Crystal Superalloy

The Effect of Stress Gradient on the Formation of TCP Phases in a Ni-based Single Crystal Superalloy at 1050 Oc

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

Experimental and Numerical Studies on Recrystallization Behavior of Single-Crystal Ni-Base Superalloy

Orientation and temperature dependence of yielding and deformation behavior of a nickel-base single crystal superalloy

Experimental Investigation on Recrystallization Mechanism of a Ni-base Single Crystal Superalloy

The Dependence of Stress and Strain Rate on the Deformation Behavior of a Ni‐based Single Crystal Superalloy at 1050°C

Influence of Cooling Rate on the Formation of Bimodal Microstructures in Nickel-Base Superalloys During Continuous Two-Step Aging

The Effect of Strain Rate on the Tensile Deformation Behavior of Single Crystal, Ni-Based Superalloys

Lattice Rotation and Deformation Mechanisms under Tensile Loading in a Single-Crystal Superalloy with [001] Misorientation

Stress-induced influence on the evolution of γ′ phase in dendritic area during long-term stress aging at 900 °C in Ni-based superalloy K444

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

Experimental Investigation on Plastic Strain and Recrystallization of Single Crystal Nickel Based Superalloys

Microstructure and γ′ phase evolution characteristics of novel nickel-based superalloy during compression

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Recrystallization behavior of a high γ′-fraction Ni-based single crystal superalloy induced by residual strain