Abstract:Microstructure evolution and fracture behavior of Mg-9.5Gd-0.9Zn-0.5Zr alloy subjected to different heat treatments were systematically investigated using SEM and TEM as well as tensile testing. It was found that the microstructure of the as-cast alloy consisted of α-Mg matrix, net-like eutectic compounds (α-Mg + Mg3 (Gd, Zn)), cubic GdH2 phases and lamellar 14H LPSO phases. After solution treated at 515 °C for 24 h, two different cooling processes were used to elucidate the effect of cooling rates on the precipitation microstructure. With a hot water quenching, those secondary phases were completely dissolved. Instead, grey-like patches were observed within the α-Mg matrix, which were proposed to be rod-like Zn2Zr3 phases around the α-Zr particle. In contrast, with a furnace cooling, the formation of 14H LPSO and several cubic Mg3 (Gd, Zn) phases was observed. Furthermore, after hot water quenching, the subsequent ageing treatment parameters were also optimized to be 225 °C for 48 h. In the peak-aged condition, a denser and uniform distribution of basal precipitates γ″ and several basal precipitates γ′ together with Zn2Zr3 and ZnZr2 phases were observed. The samples after the solution treatment (for both hot water quenching and furnace cooling) showed a much higher ductility than the as-cast alloy, while the tensile yield strength (TYS) and ultimate tensile strength (UTS) remained unchanged. After the peak-ageing, a significant increase in the TYS and UTS but a great loss in ductility was observed. In the as-cast alloy, the initiation of microcracks occurred from the net-like eutectic compounds, which was believed to be one of the most important reasons for the tensile fracture, and showed a co-existence of intergranular and transgranular fracture behavior. After the solution treatment, with a hot water quenching, the fracture can be mainly related with failures along contraction twins, and then showed a transgranular fracture behavior. While, with a furnace cooling, due to the presence of the kinked 14H LPSO phases, the fracture was caused by the broken of 14H LPSO phases, and then lead to a transgranular fracture. The peak-aged alloy exhibited a brittle intergranular fracture, which can be related with failures along soft precipitation free zones (PFZs).

Study on Tensile Fracture Behavior of Mg-11.21Gd-1.74Y-0.38Zr Alloy

Effect of Gd content on microstructure and properties of Mg-Gd-Y-Zr alloy

Study on Tensile Behavior at Various Temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Fracture Behavior of High Strength Mg-Gd-Y-Zr Magnesium Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Asymmetry of Tension and Compression of Mg-11Y-5Gd-2Zn-0.5Zr Magnesium Alloy at Different Temperatures

In-Situ Study of the Tensile Deformation and Fracture Modes in Peak-Aged Cast Mg-11Y-5Gd-2Zn-0.5Zr (weight Percent)

Microstructure and Mechanical Properties of Mg-12Gd-2Y-Sm-0.5Zr Alloy

Fracture behavior and mechanical properties of Mg–4Y–2Nd–1Gd–0.4Zr (wt.%) alloy at room temperature

Microstructure evolution and fracture behavior of Mg-9.5Gd-0.9Zn-0.5Zr alloy subjected to different heat treatments

Abnormal temperature effect on tensile strength of Mg-13Gd-2Y-0.5Zr alloy

Microstructure and Mechanical Properties of Mg-12Gd-2Y-1.5Sm-0.5Zr Alloy

Research on Microstructure and Mechanical Properties of Mg-10Gd-3Y-2Nd-0.5Zr Alloy

Modeling of Temperature- and Stress State-Dependent Yield and Fracture Behaviors for Mg-Gd-Y Alloy

Deformation mechanism of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy under high temperature and high strain rates

Microstructure and mechanical properties of Mg-12Gd-5Y-1Sm-0.5Zr alloy

Mechanical Behavior and Failure Mechanism of an As-Extruded Mg-11 Wt％y Alloy at Elevated Temperature

Elevated-Temperature Impact Toughness of Mg-(Gd, Y)-Zr Alloy

Microstructures and Mechanical Properties of Extruded Mg-9Gd-4Y-0.6Zr-T5 at Elevated Temperatures

The Effect of Precipitates on the Fracture Behavior and Tensile Properties of Mg–14Gd–0.5Zr (wt.%) Alloy