In-situ Transformation of Bi2WO6 to Highly Photoreactive Bi2WO6@Bi2S3 Nanoplate Via Ion Exchange
Tingting Huang,Yuhan Li,Xiaofeng Wu,Kangle Lv,Qin Li,Mei Li,Dongyun Du,Hengpeng Ye
DOI: https://doi.org/10.1016/s1872-2067(17)62913-9
IF: 16.5
2018-01-01
Chinese Journal of Catalysis
Abstract:As a two dimensional (2D) visible-light-responsive semiconductor photocatalyst, the photoreactivity of Bi2WO6 is not high enough for practical application owing to its limited response to visible light and rapid recombination of photogenerated electron-hole pairs. In this paper, 2D core-shell structured Bi2WO6@Bi2S3 nanoplates were prepared by calcination of a mixture of Bi2WO6 (1.3 g) and a certain amount of Na2S·9H2O (0–3.0 g) at 350 °C for 2 h. The reactivity of the resulting photocatalyst materials was evaluated by photocatalytic degradation of Brilliant Red X-3B (X3B), an anionic dye, under visible light irradiation (λ > 420 nm). As the amount of Na2S·9H2O was increased from 0 to 1.5 g, the degradation rate constant of X3B sharply increased from 0.40 × 10−3 to 6.6 × 10−3 min−1. The enhanced photocatalytic activity of Bi2WO6@Bi2S3 was attributed to the photosensitization of Bi2S3, which greatly extended the light-responsive range from the visible to the NIR, and the formation of a heterojunction, which retarded the recombination rate of photogenerated electron-hole pairs. However, further increases in the amount of Na2S·9H2O (from 1.5 to 3.0 g) resulted in a decrease of the photocatalytic activity of the Bi2WO6@Bi2S3 nanoplates owing to the formation of a photo-inactive NaBiS2 layer covering the Bi2WO6 surface.