Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Electrochemical Behavior and Localized Corrosion of X65 Steel in High Salt Concentration Brines with CO2 Saturated

CO2 Corrosion of Low Carbon Steel Under the Joint Effects of Time-Temperature-Salt Concentration

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

The Influence of pH on Localized Corrosion Behavior of X65 Carbon Steel in CO2-Saturated Brines

Corrosion Behavior of X65 Steel in Carbon Dioxide Solution under High Temperature and High Pressure

Effect of mechanical stress on electrochemical corrosion of X65 carbon steel in CO2 saturated brine

Electrochemical corrosion behaviour of four low-carbon steels in saline soil

The role of Cr content on the corrosion resistance of carbon steel and low-Cr steels in the CO2-saturated brine

Electrochemical Corrosion Behaviour of X70 Steel under the Action of Capillary Water in Saline Soils

Interaction between crevice and galvanic corrosion of X65 carbon steel in the CO2-saturated NaCl solution under the coupling of crevice and galvanic effects

Initial Corrosion of Steel in Cement-Based Composites in Saline Soil at 65°C

Evaluation of corrosion and erosion–corrosion behavior of X65 pipeline steel in flowing CO2-saturated electrolyte

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Cross Impact of CO2 Phase and Impurities on the Corrosion Behavior for Stainless Steel and Carbon Steel in Water-Containing Dense CO2 Environments

Some data on two purified kininogens from human plasma.

Corrosion behavior of X70 steel in the supercritical CO2 mixed with SO2 and saturated water

Impact of SO2 Concentration on the Corrosion Rate of X70 Steel and Iron in Water-Saturated Supercritical CO2 Mixed with SO2

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Corrosion and electrochemical investigations for stainless steels in molten Solar Salt: The influence of chloride impurity

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

Investigation on the initial atmospheric corrosion of mild steel in a simulated environment of industrial coastland by thin electrical resistance and electrochemical sensors