Investigating Size Effect of Anatase Phase Nano TiO2 on the Property of Cement-Based Composites

Zhen Li,Jialiang Wang,Yan Li,Xun Yuj,Baoguo Han

DOI: https://doi.org/10.1088/2053-1591/aad4e3

IF: 2.025

2018-01-01

Materials Research Express

Abstract:Anatase phase nano TiO2 (NT) with the diameter of 10 nm and 15 nm were used to modify cement-based composites. The results demonstrated that NT can enhance the compressive strength of cement-based composites cured at 28 day by 18.50%/18.42 MPa and 6.41%/6.38 MPa, respectively. Both two sizes of NT can increase the polymerization degree and the average silicate chain length of [SiO4](4-) in C-S-H. Moreover, they can decrease the CH orientations, restrict the CH size and endow the cement-based composites with more compact microstructure. Hence, the flexural strengths and the flexural strength to compressive strength ratios of cement-based composites cured at 3 day and 28 day have been significantly increased. Based on the nucleation free energy theory, the number of nucleating points of 10 nm NT is more than that of 15 nm NT, and the energy needed to be nucleated for each nucleating point of 10 nm is less than that of 15 nm NT. Therefore, the nucleation effect caused by 10 nm is greater than that caused by 15 nm NT and the enhancement effect of 10 nm NT on the mechanical property of cement-based composites was better than that of 15 nm NT at the same content and curing age.