Abstract:Poly(lactic-co-glycolic acid) (PLGA) is a widely used polymeric biomaterial due to its excellent biocompatibility and biodegradation. Asymmetric PLGA hollow fiber membranes (HFMs) have been extensively used as porous tubular scaffolds for tissue engineering, e.g. for nerve conduits and artificial blood vessels. PLGA HFMs are generally fabricated through a dry-jet wet spinning process, and the porous morphology of PLGA HFMs induced by polymer/solvent/nonsolvent ternary phase inversion plays a key role in their biomedical performance. In this study, PLGA was dissolved in dimethyl sulfoxide (DMSO) as the dope fluid, and deionized water with different DMSO contents was used as the bore fluid. The influence of bore fluid composition on the HFM morphology and performance was investigated by measuring phase separation time, porosity, mechanical properties, and in vitro hydrolytic degradation. The results indicated that with increased bore fluid DMSO content, the inner and outer diameters, as well as the wall thickness of the HFMs, decreased significantly; also, the inner surface became more porous and the inner surface pore size and porosity increased. Cross-sectional SEM images showed that the middle layer of the five-layered microstructure gradually changed from large voids to finger-like microvoids when the DMSO content in bore fluid increased from 0% to 60%. Furthermore, the HFMs resulting from higher DMSO content in bore fluid had a lower porosity, a faster degradation rate, a higher Young's modulus, and a lower suture retention strength. More importantly, the in vitro cell culture on the inner surface of PLGA HFMs showed that PC12 cells cultured on HFMs prepared with 60% DMSO bore fluid exhibited better cell adhesion, longer neurite length, and alignment along the HFM longitudinal axis. A ternary phase diagram and the Flory-Huggins theory were applied to analyze HFM morphological formation. The study contributes to understanding of the mechanism of HFM porous morphology formation and should guide potential application of PLGA HFMs as tissue engineering scaffolds.

Effect of Mixed Solvents on the Thermal Properties of Poly(l-Lactic Acid) (PLLA) Solution and Micromorphology of Porous PLLA Scaffolds

Blending Effects on Polymorphic Crystallization of Poly(l-lactide)

Fractionated Crystallization Kinetics and Polymorphic Homocrystalline Structure of Poly(L-lactic Acid)/poly(d-Lactic Acid) Blends: Effect of Blend Ratio

Effect of 1,4‐dioxane on Synthesis of Macroporous Poly(n‐isopropylacrylamide) Hydrogels

Polymorphous Crystallization And Multiple Melting Behavior Of Poly(L-Lactide): Molecular Weight Dependence

Porous Morphology and Mechanical Properties of Poly(lactide-Co-glycolide) Hollow Fiber Membranes Governed by Ternary-Phase Inversion

Effect of Bore Fluid Composition on Poly(lactic-Co-glycolic Acid) Hollow Fiber Membranes Fabricated by Dry-Jet Wet Spinning

Microstructure and Mechanical Properties of Poly(l‐lactide) Scaffolds Fabricated by Gelatin Particle Leaching Method

PLLA Morphology Controlled by Dry-cast Process

Study on Preparation and Morphology Structure of PLLA Cell Scaffold

Effect of POSS-NH2-grafted different plasticizers on the crystallization properties of SC-Poly (l-lactic acid)

DEGRADATION STUDY OF POLY(LACTIC ACID) POROUS SCAFFOLD AT DIFFERENT TEMPERATURES

Sex hormones, bone changes and osteoarthritis in DBA-2JN mice.

Effect of the Solvents on the Solution Mixture Derived Polylactide/Hydroxyapatite Composites

Effect of Stereocomplexation on High-temperature Microcellular Foaming Behaviour, Compressive Property and Heat Resistance of Branched Poly(l-lactide)/poly(d-lactide)

Effect of Poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) on the Crystalline Properties of Poly (L-lactic acid)

Relationship between the Stereocomplex Crystallization Behavior and Mechanical Properties of PLLA/PDLA Blends

Synergistic effects of chain dynamics and enantiomeric interaction on the crystallization in PDLA/PLLA mixtures

Scalable Preparation of Complete Stereo-Complexation Polylactic Acid Fiber and Its Hydrolysis Resistance

Specially Elaborated Thermally Induced Phase Separation to Fabricate Poly(L-Lactic Acid) Scaffolds with Ultra Large Pores and Good Interconnectivity

Macroporous and nanofibrous poly(lactide-co-glycolide)(50/50) scaffolds via phase separation combined with particle-leaching