Microstructure, Mechanical Properties and Deformation Behavior of New V-free Low-Cost Ti-6Al-xFe-yCr Alloys

Bowen Zheng,Fuyu Dong,Yue Zhang,Hongjun Huang,Xiaoguang Yuan,Xiaojiao Zuo,Liangshun Luo,Yanqing Su,Liang Wang,Baoshuai Han,Yanjin Xu

DOI: https://doi.org/10.1088/2053-1591/aaef43

IF: 2.025

2019-01-01

Materials Research Express

Abstract:A variety of low-cost V-free near-beta titanium alloys, Ti-6Al-xFe-yCr(x = 1,2 and y = 9, 12 wt%), were designed and fabricated to research the influence of Fe and Cr content on the phase composition, microstructure and properties of the alloy. The Ti-6Al-xFe-yCr alloy is less costly to prepare than the commonly used Ti-6Al-4V alloy, which exhibited a typical near-beta microstructure. When the Fe content was 2 wt% and the Cr content was 12 wt%, the resulting alloy's microstructure exhibited a great amount of beta phase and a small quantity of alpha phase, which suggested the addition of Fe and Cr was an effective method to restrain a phase formation, thereby making efforts to stabilize beta phase. To study the hot workability of the Ti-6Al-2Fe-12Cr titanium alloy, the thermal compress deformation behavior was studied at the strain rate ranging from 0.001 s(-1) to 5 s(-1), in the temperature variation of 800 degrees C up to 950 degrees C. The results showed that the thermal deformation behavior of the Ti-6Al-2Fe-12Cr alloy was susceptible to the deformation temperature and strain rate. The peak flow stress reduced as experimental temperature increment and the strain rate decrement. A constitutive model of the Ti-6Al-2Fe-12Cr alloy during thermal deformation was obtained based on the Arrhenius equation.