Abstract:Three types of polyacrylonitrile (PAN) were considered in order to investigate the effect of molecular composition and configuration on the formation of conjugated structures during stabilization and the conversion of that to pseudo-graphite sheets after carbonization. The stabilization process was performed in an inert or oxidative atmosphere with a temperature ramp from 180°Cto 280°C. The thermal behavior was studied by differential scanning calorimetry, and the change of chemical groups and conjugated structures was detected by in situ measurement of infrared (Fourier transform infrared) and ultraviolet–visible spectroscopy, respectively. The carbonization process of the stabilized samples was performed using a thermogravimetric analyzer under nitrogen atmosphere in the temperature range of 150°C–1200°C, and Raman spectra were applied to study the pseudo-graphite sheets of the residuals. It is suggested that the introduction of comonomer or the improvement of the isotactic regularity of the polymer chain are helpful to promote the stabilization reactions and accelerate the formation of conjugated structures rather than the extent of conjugation during stabilization in nitrogen. Moreover, they are also beneficial to obtain higher degree of graphitization and larger size of the pseudo-graphite sheets with less structural defects after carbonization. While stabilization is performed in air, atactic PAN copolymer has the highest extent of stabilization among these three PAN samples, but they are extremely close. PAN samples with comonomer or higher isotacticity still show a little advantage in the formation speed of the conjugated structures. After carbonization, PAN with higher isotacticity has the highest carbon yield and graphitization degree and the largest size of pseudo-graphite sheets with least structural defects. In addition, the presence of oxygen during stabilization is contributory to increase the extent of stabilization and generate some bigger conjugated structures, which leads to obtain higher graphitization degree and larger size of pseudo-graphite sheets, but it also brings more structural defects.

Accelerating Thermal Stabilization by Pyrolytic Lignin for Partially Bio‐Based Carbon Fiber Precursor

Accelerating the formation of the conjugated ladder structure of Poly(acrylonitrile-co-vinyl acetate) by cross-linked poplar lignin doped with boron phosphate

On the structural changes, mechanism and kinetics of stabilization of lignin blended polyacrylonitrile copolymer fiber

Insight into stabilization behaviors of Lignin/PAN-derived electrospun precursor fibers

Stabilization Kinetics of Gel Spun Polyacrylonitrile/lignin Blend Fiber

Effect of Polyacrylonitrile Precursor Orientation on the Structures and Properties of Thermally Stabilized Carbon Fiber

Effect of Stretching on the Orientation Structure and Reaction Behavior of PAN Fiber During the Thermal Stabilization

The formation of conjugated structure and its transformation to pseudo-graphite structure during thermal treatment of polyacrylonitrile

Comparative investigation on the thermal degradation and stabilization of carbon fiber precursors

Preparation, Stabilization and Carbonization of a Novel Polyacrylonitrile-Based Carbon Fiber Precursor

Mesophase Pitch-Based Carbon Fibers: Accelerated Stabilization of Pitch Fibers under Effective Plasma Irradiation-Assisted Modification

Chemical Structure Evolution and Mechanism During Pre-Carbonization of PAN-based Stabilized Fiber in the Temperature Range of 350–600 °C

Effect of Torrefaction Temperature on Lignin Macromolecule and Product Distribution from HZSM-5 Catalytic Pyrolysis

Structural Transformation of Polyacrylonitrile (PAN) Fibers during Rapid Thermal Pretreatment in Nitrogen Atmosphere

Dry-Jet Wet Spinning of Thermally Stable Lignin-Textile Grade Polyacrylonitrile Fibers Regenerated from Chloride-Based Ionic Liquids Compounds

Multi‐step heating strategy during thermal stabilization of polyacrylonitrile multi‐filament bundle before carbonization

Preparation of a Novel Stabilizer and Its Thermal‐oxidative Stabilization Effect on Polyamide 6

Rapid and Continuous Preparation of Polyacrylonitrile-Based Carbon Fibers with Electron-Beam Irradiation Pretreatment

Stabilization Study of Polyacrylonitrile/Cellulose Nanocrystals Composite Fibers

Processing, Structure, and Properties of Lignin- and CNT-Incorporated Polyacrylonitrile-Based Carbon Fibers

Oxidative Stabilization of Pan/Vgcf Composite