Fatigue Crack Propagation and Failure Mechanism of 13Cr-L80 Tubing in Deep-Sea Natural Gas Hydrate Exploitation
Xiaoqiang Guo,Xinghan Chen,Ning Hu
DOI: https://doi.org/10.1007/s11665-024-10516-4
IF: 2.3
2024-12-05
Journal of Materials Engineering and Performance
Abstract:To address the problem of the propagation of corrosion–fatigue cracks in tubing strings in deep-sea natural gas hydrate exploitation, a corrosion–fatigue crack propagation test of high-strength 13Cr-L80 material was conducted, and the effects of the stress ratio, load, loading frequency, and completion fluid density on the crack propagation life of a tubing string were investigated. The results demonstrate that as the stress ratio increases, the fatigue crack growth rate of the tubing string increases; however, the range of the stress intensity factor decreases, resulting in an increase in the fatigue life. When the external load was less than the critical load, the crack propagation rate decreased with increase in external load. When the 13Cr-L80 material is subjected to external alternating stress in a complex phosphate completion fluid environment, the loading frequency is higher, the crack propagation rate of the tubing string is faster, and the fatigue life is shorter. Fourth, in the low-density completion fluid, the crack propagation rate of the tubing string decreases, and the fatigue life is extended. Therefore, maintaining a stress ratio in the range of 0.2 ~ 0.25, proper heat treatment or shot peening strengthening, adjusting the loading frequency in the range of 0.6 Hz ~ 0.9 Hz, and properly reducing the completion fluid density (controlled between 1100 kg/m 3 and 1300 kg/m 3 ) can effectively improve the fatigue life of the tubing string in deep-sea natural gas hydrate exploitation.
materials science, multidisciplinary