Abstract:Al 2 O 3 thin films were deposited on the surfaces of LiFePO 4 cathodes via atomic layer deposition (ALD). Electrochemical characterization was used to evaluate the performance improvement of the cathodes coated with the ALD Al 2 O 3 thin films. In rate capability tests, an electrode coated with five ALD cycles of the Al 2 O 3 thin film exhibited the best rate performance among the tested samples when the current rate was lower than 2 C. An electrode coated with 15 ALD cycles of the Al 2 O 3 thin film delivered the highest average specific capacity—88.9 and 61.3 mAh/g at current rates of 5 C and 10 C, respectively—whereas a bare LiFePO 4 electrode did not have any capacity at the 10 C rate. These results indicate that the Al 2 O 3 coating can increase the cathode capacity at high current rates. In a cyclability test, the electrode coated with 15 ALD cycles of the Al 2 O 3 thin film retained the largest capacity after 1000 cycles at a rate of 1 C. The specific capacity of the 15ALD sample at the 1000th cycle was approximately 68% of the capacity at the first cycle, whereas this ratio was reduced to 37% for the bare LiFePO 4 electrode. These results indicate that the Al 2 O 3 coating maintains the cathode capacity after many cycles. Thicker Al 2 O 3 coatings result in a high degree of polarization and increased electrode resistance; therefore, the electrode coated with 25 ALD cycles of the Al 2 O 3 thin film exhibited a poorer rate and cycle performance than the 15ALD and 20ALD electrodes. Electrochemical impedance spectroscopy measurements and calculation of the Li + diffusion coefficient revealed that the D Li of the bare LiFePO 4 electrode was severely reduced after 1000 cycles relative to the electrode coated with 15 ALD cycles of the Al 2 O 3 thin film. This led to a faster decay in the capacity of the bare LiFePO 4 electrode after a long-duration test compared with the electrode coated with 15 ALD cycles of the Al 2 O 3 thin film. We conclude that the rate capability and cyclability of the LiFePO 4 electrode can be enhanced by depositing Al 2 O 3 ALD thin films on its surface. Under the conditions of our ALD process and electrochemical tests, 15 was found to be the optimal number of ALD cycles.

Effects of Coating Carbon Aluminum Foil on the Battery Performance

Carbon Black/graphene-Modified Aluminum Foil Cathode Current Collectors for Lithium Ion Batteries with Enhanced Electrochemical Performances

Composite Graphene‐Modified Aluminum Foil Cathode Current Collectors for Lithium‐ion Battery with Enhanced Mechanical and Electrochemical Performances

High Power Density & Energy Density Li-ion Battery with Aluminum Foam Enhanced Electrode: Fabrication and Simulation

Study of the coating effect of mildly oxidized graphene on aluminium current collectors by electrophoretic deposition and drop-casting methods for Li-ion battery application

Effect of Carbon-Coating on Internal Resistance and Performance of Lithium Iron Phosphate Batteries

Improve the Overall Performances of Lithium Ion Batteries by A Facile Method of Modifying the Surface of Cu Current Collector with Carbon

Aluminium behaviour in preparation process of lithium iron phosphate and its effects on material electrochemical performance

Full-Cell Cycling of a Self-Supporting Aluminum Foil Anode with a Phosphate Conversion Coating

Single-material Aluminum Foil As Anodes Enabling High-Performance Lithium-Ion Batteries: the Roles of Prelithiation and Working Mechanism

Effect of carbon coating on the electrochemical performance of LiFePO4/C as cathode materials for aqueous electrolyte lithium-ion battery

Graphene‐Armored Aluminum Foil with Enhanced Anticorrosion Performance As Current Collectors for Lithium‐Ion Battery

Study on anti-corrosion of heat pretreated Al foil as current collector for cathode

Structure and Electrochemical Performance of LiFePO4/C Cathode Materials Coated with Nano Al2O3 for Lithium-ion Battery

Organic carbonized copper foil facilitates the performance of current collector for lithium-ion batteries

Enhanced cyclability of lithium-ion batteries resulting from atomic layer deposition of Al2O3 on LiFePO4 electrodes

Synthesis and characterization of LiFePO_4 coating with aluminum doped zinc oxide

Interfacial effect of nano Al2O3 modifying LiFePO4 to improve capacity retention and rate capability of lithium ion batteries

Thin Aluminum Film Improving the Cycle Performance of Positive Electrode of Lithium Ion Battery

Alf3 Coating Of Lini0.5mn1.5o4 For High-Performance Li-Ion Batteries

Structure and Electrochemical Performance of LiFePO_4/C Cathode Materials Coated with Nano Al_2O_3for Lithium-ion Battery