Abstract:Cu-BTC (HKUST-1) metal-organic framework (MOF) in crystalline powder form was prepared by using a copper mesh as the metal source without involving any additional metal precursor, and its performance was evaluated for CO2 capture. The crystalline structure, morphology, textural characteristics and surface chemical properties of the synthesized HKUST-1 samples were examined by XRD, SEM, N2 physisorption, and FTIR. The MOF synthesized using the salt-free method exhibited high crystallinity, small size (∼2 μm) and uniform crystal morphology, and mesoporosity. The CO2 adsorption on the MOF was assessed at various temperatures and evaluated with respect to capacity, selectivity, kinetics, and heat of adsorption. Compared to HKUST-1 synthesized by the conventional method, the mesh-derived MOF exhibited a higher CO2 adsorption capacity (48% higher at 1 bar and 25 °C), increase in CO2/N2 adsorptive selectivity (∼11%), as well as faster adsorption kinetics (by 73%). The heat of adsorption was found to increase as well particularly at higher coverages. The obtained CO2 uptake (∼5.2 mmol/g at 1 bar and 25 °C) is among the highest reported for this MOF. The synthesis procedure presented here encompasses high yield (up to 85%), while it requires fewer chemicals and generates less waste compared to the solvothermal approach. As such, it holds the potential to facilitate scaled-up production in a cost-effective and greener way, as the demand for highly efficient porous materials for gas adsorption applications, including CO2 capture and H2 storage, is anticipated to significantly increase in the near future.

Soft-templating Synthesis of Mesoporous Metal-Organic Frameworks with Enhanced Toluene Adsorption Capacity

Facile Fabricating Hierarchically Porous Metal–Organic Frameworks Via a Template-Free Strategy

Transformation of Metal-Organic Frameworks for Molecular Sieving Membranes

Templated Fabrication of Hierarchically Porous Metal–organic Frameworks and Simulation of Crystal Growth

Construction of hierarchically porous metal-organic framework particle by a facile MOF-template strategy

Highly Enhanced Gas Uptake and Selectivity Via Incorporating Methoxy Groups into a Microporous Metal–Organic Framework

Controlled Synthesis of Metal-Organic Frameworks in Scalable Open-Porous Contactor for Maximizing Carbon Capture Efficiency

Synthesis of Hierarchically Structured Metal - Organic Frameworks by a Dual-Functional Surfactant

Template-Mediated Synthesis of Hierarchically Porous Metal–Organic Frameworks for Efficient CO2/N2 Separation

Synthesis of Hierarchical-Porous Fluorinated Metal-Organic Frameworks with Superior Toluene Adsorption Properties

Facile Synthesis of Hierarchical Porous Metal-Organic Frameworks with Enhanced Catalytic Activity

Mesoporous Hexanuclear Copper Cluster-Based Metal-Organic Framework with Highly Selective Adsorption of Gas and Organic Dye Molecules

Template-Free Synthesis Of Hierarchical Porous Metal-Organic Frameworks

Rational Design and Synthesis of a Highly Porous Copper-Based Interpenetrated Metal-Organic Framework for High CO2 and H2 Adsorption.

Hierarchically porous metal-organic frameworks: rapid synthesis and enhanced gas storage

Template Synthesis of Hierarchical Porous Metal–organic Frameworks with Tunable Porosity

CO2 Adsorption of Metal Organic Framework Material Cu-BTC via Different Preparation Routes

Mesoporous Metal–Organic Frameworks with Size‐, Shape‐, and Space‐Distribution‐Controlled Pore Structure

An Ethynyl-Modified Interpenetrated Metal-Organic Framework for Highly Efficient Selective Gas Adsorption

Room-Temperature Rapid Synthesis of Two-Dimensional Metal–Organic Framework Nanosheets with Tunable Hierarchical Porosity for Enhanced Adsorption Desulfurization Performance

Salt-free synthesis of Cu-BTC metal-organic framework exhibiting mesoporosity and enhanced carbon dioxide adsorption