Abstract:Cr(VI) as a toxic heavy metal can endanger human physical and mental health. The adsorption method has been widely used for Cr(VI) removal due to its advantages of cost-effectiveness and simplicity of operation. However, the key to Cr(VI) removal by adsorption lies in the construction of adsorption active sites. In this study, Fe 3 O 4 @COF-MT@PPy magnetic composites were prepared by the Schiff base method and in situ polymerisation to construct adsorbents with high specific surface area and abundant amino active sites for the removal of Cr(VI) from wastewater. The TEM and BET results showed that PPy was successfully encapsulated on the Fe 3 O 4 @COF-MT material, and the COF layer provided sites for the polymerisation of PPy, which resulted in a large specific surface area (400.93 m 2 /g) for Fe 3 O 4 @COF-MT@PPy, thus providing more adsorption sites. The VSM results showed that the prepared composites have good magnetic properties (13.8 emu/g) and are easy to separate from aqueous solutions. Encouragingly, the Fe 3 O 4 @COF-MT@PPy composites showed excellent adsorption performance for Cr(VI) in aqueous solution. The maximum adsorption capacity of the material for Cr(VI) was 429.18 mg/g at 298 K, which was much higher than Fe 3 O 4 @COF-MT with Fe 3 O 4 @PPy. Adsorption kinetics and isotherm analyses showed that the adsorption process was more in line with the pseudo-second-order and Langmuir models. The Fe 3 O 4 @COF-MT@PPy composites were able to maintain high adsorption capacity of Cr(VI) after five regenerations, which showed good reusability. In addition, interfering ion experiments demonstrated the selective adsorption of Fe 3 O 4 @COF-MT@PPy on Cr(VI). Using XPS for the analysis, it can be speculated that the adsorption mechanism is due to the abundant amino groups on the surface of the adsorbent firstly exerting electrostatic attraction and ion-exchange effect on the anion Cr(VI), and then the protonated amino groups reduce part of the Cr(VI) to Cr(III), and finally adsorb the Cr(III) on the surface of the material by chelation. Therefore, the recyclable Fe 3 O 4 @COF-MT@PPy has a good potential for adsorption of Cr-containing wastewater.

Improved Removal of Cr(VI) Using Fe 3 O 4 /C Magnetic Nanocomposites Derived from Potassium Fulvic Acid

Constructing Carbon-Coated Fe3O4 Hierarchical Microstructures with a Porous Structure and Their Excellent Cr(VI) Ion Removal Properties

Efficient Removal of Cr(VI) Ions in Petrochemical Wastewater Using Fe3O4@Saccharomyces cerevisiae Magnetic Nanocomposite

Magnetic graphene-based nanocomposites as highly efficient absorbents for Cr(VI) removal from wastewater

Hydrothermal synthesis of Zr-doped chitosan carbon-shell protected magnetic composites (Zr–Fe 3 O 4 @C) for stable removal of Cr(VI) from water: Enhanced adsorption and pH adaptability

Removal of Hexavalent Chromium from Wastewater by Cu/Fe Bimetallic Nanoparticles

Electrospun carbon/iron nanofibers: The catalytic effects of iron and application in Cr(VI) removal

A novel ternary magnetic Fe3O4/g-C3N4/Carbon layer composite for efficient removal of Cr (VI): A combined approach using both batch experiments and theoretical calculation

Synthesis of Magnetic Core–shell Iron Nanochains for Potential Applications in Cr(VI) Ion Pollution Treatment

Iron-carbon Composite from Carbonization of Iron-Crosslinked Sodium Alginate for Cr(VI) Removal

Synthesis of novel magnetic activated carbon for effective Cr(VI) removal via synergistic adsorption and chemical reduction

Enhanced Adsorptive Removal of Cr (VI) from Plating Industry Wastewater Using CoFe2O4/CTAB Magnetic Nanocomposites

Effective adsorption and removal of Cr(VI) from wastewater using magnetic composites prepared by synergistic effect of polypyrrole and covalent organic frameworks

Magnetic Fe3O4 assembled on nZVI supported on activated carbon fiber for Cr(VI) and Cu(II) removal from aqueous solution through a permeable reactive column

One-Step Fabrication of Recyclable Konjac Glucomannan-Based Magnetic Nanoparticles for Highly Efficient Cr(VI) Adsorption

Enhanced Cr (VI) removal by hierarchical CoFe2O4@SiO2-NH2 via reduction and electrostatic adsorption effect

Study of the Properties and Mechanism of Deep Reduction and Efficient Adsorption of Cr(VI) by Low-Cost Fe3O4-modified Ceramsite.

Fe(0)-Fe3O4 Nanocomposites Embedded Polyvinyl Alcohol/sodium Alginate Beads for Chromium (VI) Removal.

CTAB-surface-functionalized magnetic MOF@MOF composite adsorbent for Cr(VI) efficient removal from aqueous solution

Self-assembled morphology-controlled hierarchical Fe3O4 @LDH for Cr(VI) removal

Synthesis of a Multifunctional Graphene Oxide-Based Magnetic Nanocomposite for Efficient Removal of Cr(VI).