Abstract:After the extraction of molybdenum from the spent HDS catalyst, a residue containing aluminum, nickel, cobalt, and a small amount of molybdenum was obtained. The simultaneous recovery of nickel, cobalt, aluminum, and residual molybdenum from molybdenum leach residue can be achieved through hydrochloric acid leaching. In the work presented herein, the extraction of molybdenum, cobalt, and nickel from the acidic leach solution of molybdenum leach residue was investigated. Trioctyl tertiary amine can selectively extract cobalt and molybdenum from the acidic leach solution, the extraction of both cobalt and molybdenum reached more than 99% after two-stage countercurrent extraction. The combination of pure water and 25% ammonia water can be utilised for the separation and extraction of cobalt and molybdenum from the loaded cobalt-molybdenum organic phase. After the extraction of cobalt and molybdenum, a synergistic extraction system comprising decyl 4-picolinate and dinonylnaphthalene sulfonic acid can be employed for nickel extraction, achieving a nickel extraction exceeding 99.70% while maintaining aluminum extraction at only 0.32% after undergoing four-stage countercurrent extraction. The nickel stripping efficiency can reach 99.50% after four-stage countercurrent stripping, using a stripping agent of 2 mol/L H 2 SO 4 . Après l'extraction du molybdène du catalyseur HDS usé, on a obtenu un résidu contenant de l'aluminium, du nickel, du cobalt et une petite quantité de molybdène. On peut obtenir la récupération simultanée du nickel, du cobalt, de l'aluminium et du molybdène résiduel à partir des résidus d'attaque du molybdène grâce a une lixiviation à l'acide chlorhydrique. Dans le travail présenté ici, on a examiné l'extraction du molybdène, du cobalt et du nickel de la solution d'attaque acide des résidus d'attaque du molybdène. L'amine de trioctyle tertiaire peut extraire sélectivement le cobalt et le molybdène de la solution d'attaque acide, l'extraction du cobalt et du molybdène atteignant plus de 99% après une extraction à contre-courant en deux étapes. On peut utiliser la combinaison d'eau pure et de 25% d'eau ammoniaquée pour la séparation et l'extraction du cobalt et du molybdène de la phase organique chargée de cobalt-molybdène. Après l'extraction du cobalt et du molybdène, on peut utiliser un système d'extraction synergique comprenant du picolinate-4 décyle et de l'acide sulfonique dinonylnaphthalène pour l'extraction de nickel, obtenant une extraction du nickel dépassant 99.70% tout en maintenant l'extraction de l'aluminium à seulement 0.32% après avoir subi une extraction à contre-courant en quatre étapes. L'efficacité de l'élimination du nickel peut atteindre 99.50% après l'élimination à contre-courant en quatre étapes, en utilisant un agent d'élimination de 2 mol/L H 2 SO 4 .

Recovery of Aluminum from Molybdenum Extraction Residue of Spent Hydrodesulfurization Catalyst

Extraction of Molybdenum from Spent HDS Catalyst by Pressure Alkaline Leaching

Ultrasound-assisted Oil Removal of Γ-Al2o3-based Spent Hydrodesulfurization Catalyst and Microwave Roasting Recovery of Metal Mo.

Extraction of molybdenum, cobalt, and nickel from acidic leach solution of molybdenum leach residue of spent hydrodesulfurization catalyst

Recovering valuable metals from spent hydrodesulfurization catalyst via blank roasting and alkaline leaching

Removal Mechanism of Mineral Impurities in Molybdenum Concentrate Treatment Process

Highly efficient recovery of molybdenum from spent catalyst by optimized process.

Separation of V (V) and Mo (VI) in roasting-water leaching solution of spent hydrodesulfurization catalyst by co-extraction using P507 - N235 extractant

Negligible emissions and highly efficient recovery of Mo, V, and Al from spent hydroprocessing catalysts through alkaline leaching and solvent extraction

Recovery of nickel and molybdate from ammoniacal leach liquor of spent hydrodesulfurization catalyst using LIX84 extraction

Stepwise separation and recovery of molybdenum, vanadium, and nickel from spent hydrogenation catalyst

Microwave Sodium Roasting (MWSR) Spent HDS Catalysts for Recovery Mo and in Situ Sulfur Fixation

Recovery and Regeneration of Al 2 O 3 with a High Specific Surface Area from Spent Hydrodesulfurization Catalyst CoMo/Al 2 O 3

Evaluation of molybdenum recovery from sulfur removed spent catalyst using leaching and solvent extraction

Separation and Recovery of Vanadium, Nickel, and Aluminum from Acid Leaching Solution of Spent Hydrodesulfurization Catalyst by a Solvent Extraction-Oxalic Acid Precipitation Process

Economical and efficient recovery of Pd and Al2O3 from spent Pd/Al2O3 catalyst with integrated sodium roasting−reductive leaching process

Research on removal of iron and copper from low-grade molybdenum calcine in strong acid system

Synchronous conversion and targeted separation of valuable metals from spent hydroprocessing catalysts

Mechanism study of synergistic aluminum extraction and purification by ammonium for high-value conversion of secondary aluminum dross

Oil Removal of Spent Hydrotreating Catalyst Como/Al2o3 Via A Facile Method with Enhanced Metal Recovery

Sustainable recovery of surface-deposited oils and valuable metals from uncrushed spent hydroprocessing catalysts