Abstract:Ceramic coatings with aluminum titanuate (Al2TiO5) were prepared on Ti–6Al–4V alloy using pulsed bi-polar Micro-arc Oxidation (MAO). The micromorphology and phase composition of the micro-arc-oxidition ceramic coatings on the titanium alloy were characterized by X-ray powder diffraction (XRD), and scanning electron microscopy (SEM) respectively. The results revealed that the distinct discharge channels and pores on the surface of the micro-arc-oxidition coatings appeared, and these channels were connected in the molten state. The electrolyte concentration was inversely proportional to the coating hardness; additionally, the coating prepared with sodium aluminate and sodium hypophosphite concentrations of 4 g/L and 0.5 g/L, respectively, was the most refined after high-temperature sintering, and it was demonstrated to better prevent oxidation. Increasing the electrolyte concentration coincided with fluctuating coating thermal shock resistance. The thermal shock resistance of the coating respectively prepared with sodium aluminate, and the sodium hypophosphite concentrations of 4 g/L and 0.5 g/L was the highest. Additionally, the high-concentration coatings performed significantly better than the low-concentration coatings. The oxidation resistance of the coating samples was also significantly higher than that of the TC4 titanium alloy substrate. The adhesion strength between the coatings and the substrate with and without the sealing treatment was measured by tensile tests. Then, the high-temperature oxidation performance of the coating samples with and without the sealing treatment was investigated by conducting a high-temperature oxidation experiment at a calcinating temperature of 500 °C. The results indicate that the adhesion strength between the coatings and substrate was high for the as-prepared and sealed micro-arc oxidation samples regardless of whether they were calcined. The high-temperature oxidation mass increase curves for the sealed and unsealed coating samples calcined at 500 °C for 500 h revealed that the high-temperature-oxidation-induced mass increase of the coating samples sealed with a sodium silicate solution was much lower than that of the titanium alloy substrate. Thus, the sealing treatment significantly improved the high-temperature oxidation resistance of the TC4 titanium alloy. Lastly, the high-temperature oxidation behavior at 500 °C was analyzed and discussed.

Properties of Uv-Irradiated Tio2, Zro2, and Tio2-Zro2 Films As Pore-Sealing Layers on Micro-Arc-Oxidized Aluminum Alloys

Effect of Oxidation Time on the Structure and Properties of Ti-25Nb-3Zr-2Sn-3Mo Titanium Alloy Microarc Oxide Film Layer

Anti-Corrosion Property of Atomic Layer Deposition Films for Anodized Aluminum

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Study on the wear resistance and corrosion behaviour of self-sealed MAO/ZrO 2 coatings prepared on 7075 aluminium alloy

Characteristic of Microarc Oxidized Coatings on Titanium Alloy Formed in Electrolytes Containing Aluminate and Zro2 Particles

High-temperature oxidation resistance of ceramic coatings on titanium alloy by micro-arc oxidation in aluminate solution

Ultraviolet-Enhanced Bioactivity of Zro2 Films Prepared by Micro-Arc Oxidation

New Formation Mechanisms of Pores and Cracks in Micro-arc Oxidation Coatings on 6061 Aluminum Alloy with High Temperature Oxide Prefab Film

Changes in the Structure and Corrosion Protection Ability of Porous Anodic Oxide Films on Pure Al and Al Alloys by Pore Sealing Treatment

PERFORMANCE OF MICRO-ARC OXIDIZATION FILMS ON ALUMINIUM ALLOY 6063

Formation Mechanism of a Self-Sealing Pore Micro-Arc Oxidation Film on AM60 Magnesium Alloy

Investigation of a novel self-sealing pore micro-arc oxidation film on AM60 magnesium alloy

Improving the Corrosion Resistance of Micro-Arc Oxidization Film on AZ91D Mg Alloy through Silanization

Structure and Properties of Micro-arc Oxidation Coatings on Aluminum Alloys in NaAlO2-K2ZrF6 System

Corrosion Resistance and In Vitro Biological Properties of TiO2 on MAO-Coated AZ31 Magnesium Alloy via ALD

Improvement of Oxidation Resistance of TC4 Alloy by Microarc Oxidation with Sol-Gel SiO2 Sealing

Influence of Sealing Treatment on the Corrosion Resistance of PEO Coated Al-Zn-Mg-Cu Alloy in Various Environments

Effect of Α-Al2o3 Additive on the Microstructure and Properties of MAO Coatings Prepared on Low Carbon Steel

Effect of NaAlO2 concentrations on microstructure and corrosion resistance of Al2O3/ZrO2 coatings formed on zirconium by micro-arc oxidation

Making a Superior Oxide Corrosion Passivation Layer on Aluminum Using Ozone