Abstract:Photodeformable submicron Janus particles (JPs), containing an epoxy-based azo polymer (BP-AZ-CN) and poly(methyl methacrylate) (PMMA), were fabricated upon nonsolvent-induced phase separation. The formation of the JPs was induced by gradually adding deionized water into a tetrahydrofuran (THF) solution of both polymers. The results show that the two polymers start to precipitate from the solution at almost the same water content and immediately separate into two phases in each particle due to the strong incompatibility between the two components. After the nucleation, the sizes of the aggregates increase with increasing water content in the following growth stage. The amount of BP-AZ-CN molecules assembling into the aggregates is controlled by the water content in the medium, while the aggregation of PMMA molecules is a slow diffusion-controlled process due to the much higher molecular weight of this polymer. With a further increase in the water content in the dispersion medium, the swollen aggregates collapse to form JPs. Interestingly, when a dispersion with a water content of 50 vol % is diluted with a THF/H2O mixture with the same water content, the shapes of the JPs are significantly modified and vitrified after removal of THF through evaporation. By increasing the dilution multiples adopted to dilute the intermediate dispersions, JPs with more asymmetric shapes are obtained due to the enhanced asynchronous aggregation. Ternary phase diagrams calculated according to the Flory-Huggins theory provide a semi-quantitative description and rationalization of the phase separation behavior related to the thermodynamic factors. The differences in the transport behavior and aggregation dynamics of the two polymers are also proven to be critical for the formation of the asymmetric structures. Upon irradiation, the BP-AZ-CN compartments of JPs exhibit remarkable elongation along the electric vibrational direction of a linearly polarized laser beam at a wavelength of 488 nm.

Janus-like Hollow Polymer Spheres Prepared from Emulsion Droplets by the Solvent Evaporation Method

Janus-like Polymer Particles Prepared Via Internal Phase Separation from Emulsified Polymer/oil Droplets

Research of Styrene/Aerylonitrille/N-Phenlymaleimide Emalsion Copolymerization

Synthesis of non-collapsed hollow polymeric nanoparticles with shell thickness on the order of polymer gyration radius

Preparation of Hollow Microspheres by Dispersion Polymerization-Seeded Swelling Polymerization

Single-Hole Janus Hollow Sphere.

Preparation of hemispherical poly(4-vinylpyridine-co-butyl acrylate)/poly(styrene-co-butyl acrylate) composite microspheres by seeded preswelling emulsion polymerization

Janus Hemispheres through Controlled Polymerization-Induced Phase Separations within Wax Droplets

Self-Assembly of Rigid and Coil Polymers into Hollow Spheres in Their Common Solvent

Synthesis of composite eccentric double-shelled hollow spheres

Production of Micron-Sized Hollow Microspheres by Suspension Polymerization of St-DEGDA (diethylene Glycol Diacrylate) with Petroleum Ether (90–120 °C)

Hollow Structure and Its Analysis of Cross-linked Polystyrene Particles

Inward Template Synthesis of Intact Hollow Spheres

Preparation of Porous Polylactide Microspheres by Emulsion‐solvent Evaporation Based on Solution Induced Phase Separation

A novel approach for preparation of “cage-like” multihollow polymer microspheres through sulfonated polystyrene particles

Janus Hollow Spheres by Emulsion Interfacial Self-Assembled Sol-Gel Process.

Photodeformable Azo Polymer Janus Particles Obtained Upon Nonsolvent-Induced Phase Separation and Asynchronous Aggregation

Modeling the Solidification of O/W-Emulsion Droplet in Solvent Evaporation Technique

Production of PS-PMMA Janus particles with special morphology based on phase separation for the preparation of Pickering emulsions

Aggregation-Induced Emission Enabled Visualization of Anisotropic Seed Emulsion Polymerization to Synthesize Monodisperse Polymer Hemispheres

Fabrication of hollow silica spheres and their application in polyacrylate film forming agent