Enhancement of terbium efficiency by gallium and copper co-doping in (Pr, Nd)-Fe-B sintered magnets
Qingfang Huang,Qingzheng Jiang,Yao Shi,Sajjad Ur Rehman,Xing Wei,Ruoshu Wang,Yongjian Zhang,Deqin Xu,Dakun Chen,Zhenchen Zhong
DOI: https://doi.org/10.1016/j.jre.2022.04.012
IF: 4.632
2022-04-01
Journal of Rare Earths
Abstract:It is well known that Tb substitution for (Pr, Nd) in (Pr, Nd)-Fe-B based sintered magnetic materials is an effective way to increase intrinsic coercivity, but it is not quite clear whether the increment depends on the different matrix phases with various doping ingredient or not, which is essential to develop high quality magnets with high coercivity more efficiently and effectively with economic consumption of expensive Tb and other costly heavy rare earths. In this paper, we investigate the efficiency of Tb substitution for magnetic property in (Pr, Nd)-Fe-B sintered permanent magnets by co-doping Ga and Cu elements. It is shown that Ga and Cu co-doping can improve effectively the efficiency of Tb substitution to increase the thermal stability and the coercivity. The intrinsic coercivity increases up to 549 and 987 kA/m respectively by 1.5 wt% and 3.0 wt% Tb substitution in Ga and Cu co-doping magnets while the intrinsic coercivity increases up to only 334 and 613 kA/m respectively by the same amount of Tb substitution in non-Ga and low-Cu magnets. In other words, it demonstrates that there is about 329–366 kA/m linear equivalent enhancement of intrinsic coercivity by 1.0 wt% Tb substitution for (Pr, Nd) in Ga and Cu co-doped magnets. The temperature coefficients of both intrinsic coercivity β and remanence α at 20–150°C by 3.0 wt% Tb substitution for the magnets of Ga and Cu co-doping are –0.47%/K and –0.109%/K respectively, and in contrast those values are –0.52%/K and –0.116%/K respectively for the non-Ga and low-Cu magnets. It is the principal reason for more efficient enhancement of magnetic property by Tb substitution in the Ga and Cu co-doping magnets in which Tb atoms are expelled from triple junction phases (TJPs) to penetrate into the grain boundary phases (GB phases) and thus modify the grain boundary. It is prospected that the efficiency of Tb substitution would rely on different matrix phases with various doping constituent.Graphical abstractThe co-doping of Ga and Cu elements can reduce the triple eutectic point, which is beneficial for the penetration of Tb atoms from TJPs to the GB phases and the improvement of the coercivity.Download : Download high-res image (477KB)Download : Download full-size image
chemistry, applied