Abstract:The powders of La1-xSrxFeO3-delta (x=0.0 similar to 0.6) as fuel cells cathode materials were prepared by glycine-mtrate process (GNP). The formation of the perovskite structure and features of the crystallite for all samples have been characterized by means of FTIR, TG-DTA and XRD techniques. The chemical compatibility of the samples With Sm0.2Ce0.8O19 (SDC) has been investigated as well. The iodometric titration was used to determine the oxidation state of Fe ions and the oxygen nonstoichiometry in La1-xSrxFeO3-delta. It has been found that all samples calcined at 1 100 degrees C are perovskite structure with ABO, model. When Sr content at A-site was increased, blue shift of the IR absorption peak of B-O stretching vibration frequence was detected, which indicated that the proportion of covalent bond of the B-O was enhanced. The Fe mean valence value increased with the Sr-doping content, went through a maximum at x=0.4 and decreased with higher Sr substitution, whereas the oxygen nonstoichiometry of all compositions increased monotonously. With less than 40% of strontium addition, the electrical conductivity measured by four probe method increased as Sr content and reached maximal value at x=0.4. Further increase in doping resulted in deterioration of conducting properties. The changes of conductivity with temperature below 700 T were in accordance with the conduction mechanism of small polarons. It is noticeable that all the samples represent good chemical compatibility with SDC at 1200 degrees C for 12 h.

A Fundamental Study on the Chemical Stability of La1-xSrxCo0.2Fe0.8O3-delta Cathodes for Intermediate Temperature Solid Oxide Fuel Cells

Influence of CO2 on the Cathode Performance and Stability of La1-XSrxCo0.2Fe0.8O3-Î´ in Solid Oxide Fuel Cells

Performance Stability and Degradation Mechanism of La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3−δ Cathodes under Solid Oxide Fuel Cells Operation Conditions

Surface Modifications of Nano-Structured Cathodes to Enhance Durability of Intermediate Temperature Solid Oxide Fuel Cells

Long-term Stability of Infiltrated La0.8Sr0.2CoO3−, La0.58Sr0.4Co0.2Fe0.8O3− and SmBa0.5Sr0.5Co2.0O5+ Cathodes for Low Temperature Solid Oxide Fuel Cells

A new (La0.2Nd0.2Gd0.2Sr0.2Ba0.2)Co0.2Fe0.8O3-δ high-entropy oxide cathode for intermediate temperature solid oxide fuel cell

A Novel Cathode Material of Iron-Doping Sm0.5sr0.5coo3 for Solid Oxide Fuel Cell

Characterization And Properties Of La1-Xsrxfeo3-Delta With Perovskite-Type Structure

Effect of Atmospheric Carbon Dioxide on Surface Segregation and Phase Formation in La0.6Sr0.4Co0.2Fe0.8O3-δThin Films

Extrinsic Fe3+ Stabilized La1-XSrxCoO3-δ Thin Film Cathode for Enhanced Electrochemical Performance

Preparation, Structure and Performance of La0.6Sr0.4Co0.2Fe0.8O3 Cathodes of Intermediate Temperature Solid Oxide Fuel Cells

Structure and electrochemical properties of Sm0.5Sr0.5Co1 - xFexO3 - δ cathodes for solid oxide fuel cells

Enhanced Electrochemical Performance and Operating Stability of La0.8Sr0.2Co0.2Fe0.8O3-δ Fiber Cathode Via Gd0.2Ce0.8O1.9-δ Coating for Intermediate Temperature Solid Oxide Fuel Cells

Thermochemical Compatibility and Polarization Behaviors of La0.8Sr0.2Co0.8Ni0.2O3−δ As a Cathode Material for Solid Oxide Fuel Cell

Preparation And Characterization Of Ba0.4sr0.6co1-Xfexo3-Delta Cathode Materials

Development of La0.6Sr0.4Co0.2Fe0.8O3−δ Cathode with an Improved Stability Via La0.8Sr0.2MnO3-film Impregnation

Suppression of Sr surface segregation in La0.8Sr0.2Co0.2Fe0.8O3-delta via Nb doping in B-site

Effect of A-Site Cation Defect on Electrochemical Performance and Stability of La0.8Sr0.2Co0.2Fe0.8O3- Δ Cathode

An electron hole doping and soft x-ray spectroscopy study on La1-xSrxFe0.75Ni0.25O3-δ

Thermal and Electrical Properties of New Cathode Material Ba[sub 0.5]Sr[sub 0.5]Co[sub 0.8]Fe[sub 0.2]O[sub 3−δ] for Solid Oxide Fuel Cells

Stability Investigation for Symmetric Solid Oxide Fuel Cell with La0.4Sr0.6Co0.2Fe0.7Nb0.1O3-δElectrode