Abstract:A novel layered zirconium phosphate crystal with organic di-protonated 1,6-hexyldiamine (HDA) cation, 0.5 [Zr(PO 4)(HPO 4)]·1 5H 2O (abbreviated to γ-(HDA)ZrP), was synthesized under hydrothermal conditions and characterized by single-crystal and powder XRD, IR and TG-DTA. The crystal is in orthorhombic space group Imm2 with a= 3 433?8 nm, b= 0 533?8 nm, c= 0 662?0 nm, V= 1 213?42 nm3, Z=2, R= 0 055?4 and R W= 0 075?4. The title compound was of γ-type layered structure which was formed by corner-sharing ZrO 6 octahedron and PO 4, PO 3(OH) tetrahedron units, and the layer-to-layer distance was about 1 77 nm. The HDA molecule, which was perpendicular to the zirconium phosphate layer and bent a little like a bow, supported and connected the zirconium phosphate layer by the hydrogen bonds between the two end nitrogen atoms of HDA molecule and one of the two oxygen atoms stretching out of the zirconium phosphate layers. The water molecules occupied two positions between the layers. One was the cavities formed by HPO 2- 4 tetrahedrons on the surface of the zirconium phosphate layer, and the other was amid HDA molecules with four water molecules in one group. The XRD pattern simulated from the single crystal structure analysis result was in accordance with that collected from the powder sample synthesized. The absorption bands of organic amine and water appeared in the IR spectrum of γ-(HDA)ZrP, corroborated the crystal structure determined by XRD analysis. On heating, one and a half water molecules were lost at 180 ℃ and the HDA began to decompose at 250 ℃. After getting rid of the water molecules by heating at 220 ℃ for 3 h, no obvious change in the crystal structure was observed.

Synthesis and Characterization of A New-Type of Zirconium-Phosphate Crystal from Alcohol System

Ionothermal Synthesis and Characterization of Crystalline Zirconium Phosphate from Oxalic Acid/Tetrapropyl Ammonium Bromide System

Synthesis, Characterization and Crystal Structure Analysis of an Open-Framework Zirconium Phosphate

Synthesis and Exfoliation of Discotic Zirconium Phosphates to Obtain Colloidal Liquid Crystals

Synthesis and Characterization of Zincphosphate from Non-aqueous System

Synthesis, Structure, and Characterization of Two Photoluminescent Zirconium Phosphate-Quinoline Compounds

SYNTHESIS AND CHARACTERIZATION OF A NOVEL ZINC PHOSPHATE

Ionothermal Synthesis, Structure and Characterization of Three-Dimensional Zinc Phosphates.

Synthesis and Characterization of Layered Zirconium Phosphate Crystal with 1,6-Hexyldiamine As Template

Synthesis, Structure and Characterization of ZrPOF-DEA, a Microporous Zirconium Phosphate Framework Material

Ionothermal Synthesis and Characterization of Two Zinc Phosphates from a Protic Ionic Liquid

Synthesis and Characterization of Aluminophosphate Molecular Sieve AlPO4-41 from Alcohol Systems

Hydrothermal Synthesis, Crystal Structure and Characterization of a Two-dimensional Layered Zinc Phosphate

Solvothermal Synthesis and Characterization of the Layered Compound of Α-Zirconium Hydrophosphate

Facile Synthesis and Novel Application of Zirconia Catalyzed and Templated by Lysozyme

Syntheses and Characterization of Novel Open-framework Zinc Germanate Phosphates

Studies on Synthesis and Properties of Layered Zirconium Phosphate

Synthesis of Amorphous Supermicroporous Zirconium Phosphate Materials by Nonionic Surfactant Templating

Overcoming the crystallization and designability issues in the ultrastable zirconium phosphonate framework system

Synthesis and characterization of a new zinc phosphate with 16-ring channels: Zn3PO4(HPO4)3·C6N3H18

Synthesis of Mesoporous Zirconia with Crystalline Framework in Super-critical Ethanol