Abstract:In an attempt to synthesize novel zirconium phosphate materials, a series of syntheses have been performed in a deep eutectic solvent (DES), composed of tetrapropylammonium bromide (TPABr) and oxalic acid. As a result, this DES does not act as a template provider in reaction probably owing to the steric effects of the longer chains of the TPA cation, and only the alpha-Zr(HPO4)(2). H2O (alpha-ZrP) phase has been achieved. However, after organic amine was added to the initial reaction mixture in a normal way, the additives did act as a template to induce the zirconium phosphate framework. For example, with 1,4-dimethylpiperazine as an additive, a novel layered compound, [C6H16N2](0.5)Zr-(H0.5PO4)2. H2O (denoted as ZrPO4-DES8) was obtained. Its structure was determined from single-crystal X-ray diffraction (XRD) data and consists of zirconium phosphate layers with the protonated 1,4-dimethylpiperazine and water molecules in between. Interestingly, the two layered materials as additives in a liquid lubricant exhibit excellent friction behavior with higher load-carrying and antiwear capacities in comparison to typical lubricant additives such as MoS2 and graphite, increase the P-B value of the base oil by 27.2% and 8.5%, and decrease the wear scar diameter of the base oil by 43% and 36%, respectively. Scanning electron microscopy, XRD, and energy-dispersive X-ray spectrometry are used to investigate the lubricant behavior of those materials.

Studies on Synthesis and Properties of Layered Zirconium Phosphate

Solvothermal Synthesis and Characterization of the Layered Compound of Α-Zirconium Hydrophosphate

Hydrothermal Synthesis of Layered Α-Zirconium Phosphate Disks: Control of Aspect Ratio and Polydispersity for Nano-Architecture

Synthesis and Exfoliation of Discotic Zirconium Phosphates to Obtain Colloidal Liquid Crystals

Ionothermal Synthesis and Characterization of Crystalline Zirconium Phosphate from Oxalic Acid/Tetrapropyl Ammonium Bromide System

Disk-Shaped Colloids: the Synthesis and Applications of ZrP Crystals

Organically modification of layered alpha-zirconium phosphate

Studies on colloidization and stability of layered phosphates in amine hydrous solution

Studies on the intercalation of n-alkylamine and n-amino-alcohol in layered zirconium phosphate

Synthesis, Characterization and Crystal Structure Analysis of an Open-Framework Zirconium Phosphate

Ionothermal Synthesis Of Layered Zirconium Phosphates And Their Tribological Properties In Mineral Oil

Microwave-assisted Rapid Synthesis of Hexagonal Α-Zirconium Phosphate Nanodisks As a Pickering Emulsion Stabilizer

Hydrothermal synthesis of layered zirconium phosphates and their intercalation properties

Hydrothermal synthesis and characterization of the layered compound of alpha-titanium hydrophosphate

Studies on the Colloidization and Stability of Layered M(IV) Phosphates in Aqueous Amine Solutions

Hydrothermal Synthesis and Thermal Stability Oflayered Compound of Tetravalent Metal Phosphate

Synthesis, Structure and Characterization of ZrPOF-DEA, a Microporous Zirconium Phosphate Framework Material

Studies on preparation, characterization and catalytic properties of zirconium phenylphosphonate phosphite and its sulfonated derivatives

Preparation and Properties of Zirconia-Pillared Zirconium Phosphate and Phenylphosphonate

Alumina-pillared Α-Zirconium Phosphate Prepared by In-Situ Polymerization Method

Ionothermal synthesis of zirconium phosphates and their catalytic behavior in the selective oxidation of cyclohexane.