Abstract:The sonohydrothermal (SHT) treatment is an innovative technique allowing the simultaneous coupling of low frequency ultrasound and hydrothermal conditions for the synthesis of materials. The aim of the present work was to investigate, for the first time, the synthesis of zeolite A and its formation mechanism under SHT conditions. The zeolite synthesis was carried out under sonohydrothermal conditions using a specially designed reactor that allows the application of ultrasonic irradiation at 20 kHz in an autoclave-type reactor heated up to 200 °C under autogenous pressure. The conversion kinetics of the amorphous hydrogel to zeolite A and its further conversion to sodalite were studied. Syntheses were performed in the SHT reactor at 80 and 100 °C, varying the synthesis time from 15 minutes to several hours. The required time to obtain fully crystalline zeolite A under sonohydrothermal conditions was only 25 minutes, highlighting a significantly improved crystallization rate compared to silent conditions (a 9.6-fold kinetic gain). In addition, the resulting zeolite A has smaller particles and a more homogeneous particle size distribution than the zeolite synthesized by hydrothermal treatment. These results can be explained by the sonofragmentation of the amorphous gel and the concomitant enhanced mass transfer of the building units at the interface between the crystallite surface and the solution resulting from the acoustic cavitation activity under SHT conditions. Compared to classical hydrothermal heating, a drastic kinetic increase of the transformation of zeolite A into the more stable sodalite phase was also observed under sonohydrothermal conditions.

Synthesis of NaA Zeolite Using Diatomite as Silicon Source and Its Proton Conduction Property

Synthesis of Ultra-Fine NaA Zeolite by Low-Temperature Hydrothermal Treatment

Synthesis of NaY zeolite molecular sieves from calcined diatomite

Highly efficient synthesis of high-silica SSZ-13 zeolite by interzeolite transformation of L zeolite at higher temperature

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Synthesis zeolites in water vapour phase and their properties

Rice Husk as Raw Material in Synthesis of NaA (LTA) Zeolite

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Controllable and SDA-free synthesis of sub-micrometer sized zeolite ZSM-5. Part 1: Influence of alkalinity on the structural, particulate and chemical properties of the products

Hydrothermal/Alkali Fusion Synthesis of Zeolite NaA and NaX from Pyrophyllite Mineral Clay

SYNTHESIS AND CHARACTERIZATION OF A-TYPE ZEOLITE MEMBRANES ON ALUMINA PARTICLES SURFACE

Synthesis of NaA Zeolite Membranes Decorated by Silane

Synthesis of NaA zeolite membranes from clear solution

Synthesis of zeolite NaA membrane from fused fly ash extract

Preparation of ZSM-5 molecular sieve by diatomaceous earth in-situ crystallization

Direct Synthesis of Hierarchical LTA Zeolite Via a Low Crystallization and Growth Rate Technique in Presence of Cetyltrimethylammonium Bromide.

Synthesis and Characterization of High-Quality Zeolite LTA and FAU Single Nanocrystals

Sonohydrothermal synthesis of zeolite A and its phase transformation into sodalite