Abstract:Copper (Cu) is the only known material that can efficiently electrocatalyze CO2 to value-added multicarbon products. Owing to the instability of the Cuδ+ state and microscopic structure in reactions, Cu catalysts are still facing big challenges with low selectivity and poor durability, particularly at high current densities. Herein, we report a rational one-step surface coordination approach for the synthesis of Cu dendrites with an ultrastable Cuδ+ state and hydrophobicity (Cu CF), even after exposure to air for over 6 months. As a result, Cu CF exhibited a C2 FE of 90.6% at a partial current density of 453.3 mA cm-2 in a flow cell. A 400 h stable electrolysis at 800 mA and even a ground-breaking stable operation at a large industrial current of 10 A were achieved in the membrane electrode assembly (MEA) form. We further demonstrated a continuous production of C2H5OH solution with 90% relative purity at 600 mA over 50 h in a solid-electrolyte reactor. Spectroscopy and computation results suggested that Cu(II) carboxylate coordination species formed on the surface of Cu CF, which ensured the stability of the Cuδ+ state and hydrophobicity. As a result, rich active sites and a stable three-phase interface on the catalyst surface were achieved, along with the optimized *CO adsorption strength and adsorption configuration. The mixed *CO adsorption configurations on Cu CF made the *CO dimerization process easier, which promoted the conversion of CO2 to C2 products. This work provides a promising paradigm for the design and development of Cu-based catalysts with ultrahigh stability under industrial current densities.

Coupling of Cu(100) and (110) Facets Promotes Carbon Dioxide Conversion to Hydrocarbons and Alcohols

Stabilizing Cu0/Cu2+ Interface by Hydroxy-Rich Amorphous SiO2 for Enhanced Electrocatalytic CO2 Reduction to Ethylene

Efficient CO2 electroreduction on facet-selective copper films with high conversion rate

Efficient CO2 Electroreduction to Multicarbon Products at Cusio3/Cuo Derived Interfaces In Ordered Pores

In Situ Copper Faceting Enables Efficient CO2/CO Electrolysis

Metal Ion Cycling of Cu Foil for Selective C–C Coupling in Electrochemical CO 2 Reduction

Adjacent Copper Single Atoms Promote C-C Coupling in Electrochemical CO<sub>2</sub> Reduction for the Efficient Conversion of Ethanol

Hydrophobic, Ultrastable Cuδ+ for Robust CO2 Electroreduction to C2 Products at Ampere-Current Levels

Direct OC-CHO Coupling Towards Highly C2+ Products Selective Electroreduction over Stable Cu0/Cu2+ Interface.

Low-coordinated copper facilitates the *CH 2 CO affinity at enhanced rectifying interface of Cu/Cu 2 O for efficient CO 2 -to-multicarbon alcohols conversion

Metal ion cycling of Cu foil for selective C–C coupling in electrochemical CO2 reduction

Identification of Cu(100)/Cu(111) Interfaces As Superior Active Sites for CO Dimerization During CO2 Electroreduction.

Revealing the Nature of C-C Coupling Sites on a Cu Surface for CO2 Reduction

Direct OC-CHO coupling towards highly C 2+ products selective electroreduction over stable Cu 0 /Cu 2+ interface

Facet‐Selective Deposition of Ultrathin Al2O3 on Copper Nanocrystals for Highly Stable CO2 Electroreduction to Ethylene

Unravelling the Effect of Crystal Facet of Derived‐Copper Catalysts on the Electroreduction of Carbon Dioxide under Unified Mass Transport Condition

Facet Dopant Regulation of Cu2O Boosts Electrocatalytic CO2 Reduction to Formate

Enhanced electroreduction of CO2 to C2+ products on heterostructured Cu/oxide electrodes

Identification of Cu(100)/Cu(111) Interfaces as Superior Active Sites for CO Dimerization During CO 2 Electroreduction

Adjacent Copper Single Atoms Promote C-C Coupling in Electrochemical CO 2 Reduction for the Efficient Conversion of Ethanol

Surface/interface Reconstruction In-Situ on Cu2O Catalysts with High Exponential Facets Toward Enhanced Electrocatalysis CO2 Reduction to C2+ Products