Characterization of High–valence Mo–doped PrBaCo2O5+ Cathodes for IT–SOFCs

Jingsheng Xu,Hongdong Cai,Guodong Hao,Leilei Zhang,Zhaoyuan Song,Wen Long,Lei Zhang,Li Wang

DOI: https://doi.org/10.1016/j.jallcom.2020.155600

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:PrBaCo2-xMoxO5+delta (PrBCM-x, x = 0.00-0.07) layered perovskites were evaluated as cathodes for IT-SOFCs. The Mo solid solution limit for PrBCM-x was up to x = 0.05. Mo doping in the PrBCM-x decreased the electrical conductivity, which may mainly be due to the disturbed center dot center dot center dot Co-O-Co center dot center dot center dot electron transport channels with Mo doping. The thermal expansion coefficients decreased from 21.0 x 10(-6) K-1 at x = 0.00 to 19.0 x 10(-6) K-1 at x = 0.03 and then to 18.1 x 10(-6) K-1 at x = 0.05. Although a reduction in electrochemical performance with highevalence Mo doping into PrBaCo2O5+delta (PrBCO) was demonstrated, the reduced TECs and improved electrochemical stability were more attractive for the application of SOFC cathode. Electrochemical dynamic processes determined by EIS fitting indicated that Mo doping contributed to the rate-determining role of ion charge transfer in the oxygen reduction reaction and thus resulted in reduced electrochemical performance. By comprehensive consideration, the PrBCM-0.03 was confirmed as the most suitable cathode candidate for IT-SOFCs. The polarization resistance was 0.067 Omega cm(2) at 700 degrees C for the PrBCM-0.03 cathode on Sm0.2Ce0.8O1.9 (SDC) electrolyte. A single cell with PrBCM-0.03 cathode and 300 mu m-thick SDC electrolyte showed a maximum power density of 339 mW cm(-2) at 700 degrees C and almost no degradation in performance was detected after a 42 h testing. This study provides a preliminary basis for further research into high-valence ion doping in layered perovskite cathode materials. (C) 2020 Elsevier B.V. All rights reserved.