Abstract:The quenching sensitivity of 7A65 aluminum alloy was investigated using interrupted quenching experiments. The time–temperature transformation (TTT) and time–temperature performance (TTP) curves of the alloy were determined. The results indicate that the nose temperature is about 320 °C and the quenching sensitivity temperature range is from 240 °C to 360 °C. During the isothermal treatment, the supersaturated solid solution resolves to the equilibrium phase of η (MgZn2), and the precipitation rate is the largest at about 320 °C. Through transmission electron microscope (TEM) observation and X-ray diffraction (XRD) tests, it was found that with the extension of the isothermal holding time, the originally dispersed η’ phase gradually decreases until disappear, and the number of η phase increases and gradually grows up at the grain boundary or around the Al3Zr particles. The rod-like η phase at the grain boundary is distributed from discontinuous distribution to chain-like continuous distribution, and the precipitation free zone (PFZ) is gradually generated and widened as the holding time is extended. At the nose temperature, the driving force of nucleation is high, and the diffusion rate is fast, which promotes the precipitation and growth of η phases. The coarse η phase weakens the mechanical properties. According to the results, it is recommended to increase the cooling rate at the sensitivity temperature range to reduce the precipitation of the η phase and decrease the quenching cooling rate from solution temperature to 360 °C to reduce residual stresses in the components.

Investigation of Microstructure Evolution and Quench Sensitivity of Al–Mg–Si–Mn–Cr Alloy During Isothermal Treatment

Atomic-scale study on the precipitation behavior of an Al-Zn-Mg-Cu alloy during isochronal aging

Study on quenching sensitivity of an Al–Zn–Mg–Cu alloy containing trace amounts of Sc and Zr

TTT Curves of an Al-Mg-Si-Mn Alloy

Quench sensitivity and microstructure evolution of the 2060 Al-Cu-Li alloy with a low Mg content

Study on Quench Sensitivity during Isothermal Treatment of 7A65 Aluminum Alloy

Quench Sensitivity and Transformation Kinetics of High Vacuum Die Casting AlSi10MgMn Alloy

Microstructure and Hardness Evolution During Isothermal Process at 700 °C for Fe–24Mn–0.7Si–1.0Al TWIP Steel

Detailed investigation of quench sensitivity of 2050 Al-Cu-Li alloy by interrupted quenching method and novel end quenching method

Decreased dislocation density as an origin for the quench sensitivity of the Al-Si-Mg alloys with high Si content

Influence of Quench-Induced Precipitation on Aging Behavior of Al-Zn-Mg-Cu Alloy

Study of supersaturated solid solution decomposition during quenching of sheets from Al-Mg-Si aluminum alloy

The effect of quenching rates on microstructure and mechanical properties of an Al-Si-Cu-Mg alloy

Precipitated phase characteristics and fracture behaviour of cast Al–Cu–Mn alloy

Quench Sensitivity of 6351 Aluminum Alloy

Microstructure evolution of a novel low-silicon cast aluminum alloy modified with Mn and Cr during solution treatment

Microstructure and Mechanical Properties of Cast Al-Si-Cu-Mg-Ni-Cr Alloys: Effects of Time and Temperature on Two-Stage Solution Treatment and Ageing

Microstructure, mechanical properties and residual stress of high vacuum die casting AlSi10MgMn alloys with different spray quenching

A Comparative Study on Precipitation Behavior of a Sand-Cast Al–Li–Cu Alloy with the Different Quenching Rates

Microstructural Evolution and Mechanical Properties of Cast Al-2Li-2Cu-0.5Mg-0.2Zr Alloy During Heat Treatment

Residual stress and precipitation of Mg-5Zn-3.5Sn-1Mn-0.5Ca-0.5Cu alloy with different quenching rates