Bi(Mg2/3Nb1/3)O3 Addition Inducing High Recoverable Energy Storage Density in Lead-Free 0.65Batio3-0.35Bi0.5na0.5tio3 Bulk Ceramics

Yun Qiu,Ying Lin,Xiaoyu Liu,Haibo Yang

DOI: https://doi.org/10.1016/j.jallcom.2019.05.092

IF: 6.2

2019-01-01

Journal of Alloys and Compounds

Abstract:In this work, Bi(Mg2/3Nb1/3)O3 (BMN) was introduced to enhance the energy storage properties of 0.65BaTiO3-0.35Bi0.5Na0.5TiO3 ceramic. All of the samples were prepared by the conventional solid-state method. With increasing the dopants content, the average grain size was reduced from 0.92 μm to 0.38 μm, which consequently improves the breakdown strength (reaching 182 kV/cm). Meanwhile, the P-E loops become slimmer and slimmer and the remanent polarization is declined from 31.16 μC/cm2 to 0.62 μC/cm2. The ceramics reveal a high recoverable energy storage density of 1.6 J/cm3 and an extremely high energy efficiency of 90.3%, which are superior to those of most of lead free ceramics. The excellent energy storage performance makes the as-prepared ceramics to be candidate materials for pulsed power capacitors.