Enhanced energy storage properties in Nb-modified Bi 0.5 Na 0.5 TiO 3 –SrTiO 3 lead-free electroceramics

Xing-Ye Tong,Min-Wei Song,Jia-Jun Zhou,Ke Wang,Chun-Lin Guan,Hong Liu,Jing-Zhong Fang

DOI: https://doi.org/10.1007/s10854-019-00876-2

2019-01-01

Abstract:Lead-free (1 − x )Bi 0.5 Na 0.5 TiO 3 – x SrTiO 3 + ywt%Nb 2 O 5 electroceramics were synthesized using the conventional method to investigate the influences of SrTiO 3 content and Nb 2 O 5 doping on the material’s phase structure, microstructure, and energy storage properties. All the investigated compositions possessed a single perovskite phase structure of pseudocubic symmetry. The introduction of SrTiO 3 and Nb 2 O 5 led to a weakened relaxor characteristic and a decrease of T m . The microstructure was refined by Nb 2 O 5 doping, and the average grain size of the 0.6Bi 0.5 Na 0.5 TiO 3 –0.4SrTiO 3 sample decreased drastically from ~ 10 to ~ 1 µm when 2.5 wt% Nb 2 O 5 was added. Enhanced electrical breakdown and polarization were achieved for the samples with the refined microstructure. Among the various Bi 0.5 Na 0.5 TiO 3 -based ceramics, 0.6Bi 0.5 Na 0.5 TiO 3 –0.4SrTiO 3 + 2.5 wt%Nb 2 O 5 ceramic exhibited excellent energy-storage properties with thermal stability, in which large recoverable energy-storage density W rec ~ 1.82 J/cc and efficiency η ~ 81% were both achieved. Our results indicate that this ceramic is a promising material for lead-free energy storage applications.