High-performance direct carbon dioxide-methane solid oxide fuel cell with a structure-engineered double-layer anode
Tong Wei,Peng Qiu,Jun Yang,Lichao Jia,Bo Chi,Jian Pu,Jian Li
DOI: https://doi.org/10.1016/j.jpowsour.2020.229199
IF: 9.2
2021-02-01
Journal of Power Sources
Abstract:Reduced La0.6Sr0.2Cr0.85Ni0.15O3 (LSCrN) contains exsolved Ni nanoparticles (LSCrN@Ni) and abundant oxygen vacancies. Thus, it is an excellent catalyst for CO2 dry reforming of CH4. To use CH4 directly in solid oxide fuel cells, Ni–Ce0.9Gd0.1O1.95 (GDC) anode-supported cells are fabricated with and without a layer of LSCrN@Ni-20 wt% GDC on top of the anode, which are defined as double anode supported cell (DASC) and conventional anode supported cell (CASC), respectively. They are investigated comparatively by X-ray diffraction, thermal expansion, thermogravimetry, scanning electron microscopy, and electrochemical performance measurement in H2 and 50%CO2–50%CH4 fuels. Both CASC and DASC demonstrate similarly high performance with H2 fuel, the maximum power density is 856 and 822 mW cm−2 at 750 °C, respectively. When 50%CO2–50%CH4 is used, DASC outperforms CASC significantly, showing a maximum power density of 758 mW cm−2 and an on-cell CH4 conversion of 85.5% at 750 °C. Also, DASC demonstrates a stable performance, and the cell voltage and CH4 conversion remain unchanged at 0.65 V and 84% without detectable carbon formation in the anode, while those of CASC decrease monotonously from the beginning with observable carbon formation during a test of 36 h under 400 mA cm−2 at 750 °C.
energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical