Multifunctional conjugated molecules combined with electrospun CuCoP/carbon nanofibers as a modifier of Pt counter electrode for dye-sensitized solar cells
Fang-Sian Lin,Mani Sakthivel,Miao-Syuan Fan,Chien-Hsin Wu,Guan-Lun Fong,Jiang-Jen Lin,Ru-Jong Jeng,Kuo-Chuan Ho
DOI: https://doi.org/10.1039/d2tc01564a
IF: 6.4
2022-07-22
Journal of Materials Chemistry C
Abstract:The star-shape of 3,6-bis(5-(4,4′-bis(3-azidopropyl)-[1,1′:3′,1′-terphenyl]-5′-yl)-thien-2-yl)-2,5-bis(2-ethylhexyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione (DPPTPTA) is combined with electrospun bimetallic copper-cobalt phosphide decorated on carbon nanofibers (CuCoP/CNF) and used as a modified layer ( DPPTPTA@CuCoP/CNF ) on the platinum (Pt) coated counter electrode (CE) of dye-sensitized solar cells (DSSCs). DPPTPTA possesses ladder-like energy levels for efficient charge separation while CuCoP/CNF has a high electrocatalytic activity and sufficient electrical conductivity. Overall, the DPPTPTA@CuCoP/CNF heterostructure exhibits attractive performance needed for the CE of DSSCs. From electrochemical analysis, the DPPTPTA@CuCoP/CNF modified layer ensures efficient charge transfer at the CE/electrolyte interface with low charge transfer resistance. Moreover, the CE/electrolyte interface possesses a small electron recombination rate, since the modified layer has good charge separation ability. Under 1 sun (AM 1.5G, 100 mW cm -2 ) conditions, the pertinent DSSC achieved a photoelectric conversion efficiency ( η ) of 9.50%, open-circuit voltage ( V OC ) of 827 mV, short-circuit current density ( J SC ) of 16.25 mA cm -2 , and fill factor ( FF ) of 0.71. Under indoor conditions, the η value at 6,000 lux (1.89 mW cm -2 ) reached 25.44%. Finally, the porous three-dimensional nanofiber structure of the modified layer can ensure long-term at-rest stability (90% retention after 3,000 h). Thus, the DPPTPTA@CuCoP/CNF modified layer-based DSSC can be considered as a promising device for possible renewable energy.
materials science, multidisciplinary,physics, applied