Controlling the Chain Orientation and Crystal Form of Poly(9,9-dioctylfluorene) Films for Low-Threshold Light-Pumped Lasers

Junjie Wang,Yuchao Liu,Deyue Zou,Zhongjie Ren,Jie Lin,Xingyuan Liu,Shouke Yan

DOI: https://doi.org/10.1021/acs.macromol.0c02815

IF: 5.5

2021-04-21

Macromolecules

Abstract:Neat thin films of semiconducting polymers are attractive as efficient gain media toward optically pumped lasers. However, the optical loss and out-coupling of isotropic polymer thin films are far from being rationally regulated from the perspective of chain orientation and crystal form. Herein, we accomplished a simultaneous control of both chain orientation and crystal form in large-area highly ordered poly­(9,9-dioctylfluorene) (PFO) thin films through epitaxial crystallization. The well-arranged PFO lamellae naturally shape a low-loss, graded-index waveguide to provide spatially distributed optical feedback. Moreover, much more horizontally oriented dipoles significantly enhance the light out-coupling efficiency. Thus, the only 65 nm-thickness oriented PFO films demonstrate excellent amplified spontaneous emission with a low excitation threshold (7.1 μJ/cm2) and a narrow full width at half-maximum (2.2 nm) measured in the perpendicular direction of PFO chains. This strategy opens an effective pathway to prepare high-performance polymer thin-film lasers and electrically pumped polymer lasers.

polymer science