Abstract:In southern power grid, four 500kV composite wall bushings used at a converter station was found significantly aging after 15 years' operation, such as chalking, cracks and low hydrophobicity. The housing material of these wall bushings is liquid silicone rubber (LSR). In order to extend the service life, the out door insulation was repaired by RTV. As the internal failure, one of the four bushings was forced to be out of service. In this paper, the outer shed of the wall bushing was used to evaluate the aging characteristics of the LSR sheds after long term operation. The macroscopic aging characteristics of LSR sheds were investigated by using hydrophobicity and hydrophobicity transfer test, tensile and tear strength test. The microscopic characteristics of the aging sheds were obtained by using Scanning Electron Microsope (SEM), Fourier Transform Infrared Spectroscopy (FTIR) and X-ray Photoelectron Spectroscopy (XPS). It was found that the aging of the LSR shed developed from outer surface into the inside, and the layer structure including the chalking layer and the inner layer was obviously observed. The hydrophobicity, hydrophobicity transfer, tensile strength and tear strength of the aging sheds had different decrease. At microcosmic angle of view, the aging sheds appeared irregular shaped patches with a reduced surface roughness and adhesion; FTIR and XPS results indicated that the side chain groups of PDMS in the chalking layer were oxidized, crosslinked with other polysiloxane chains, forming more Si-O-Si groups, accompanied by the precipitation of TiO2 and white carbon black fillers. Due to the change of silicone rubber material from organic to inorganic, the content of C and Si elements in the chalking layer decreased, and the content of O element increased.The research also shows that, the hydrophobicity and hydrophobicity transfer of the aging LSR sheds can be improved by RTV repairment, but the appearance and hydrophobic changes still needs to be regularly monitored in the operation.

Aging Characteristics of GIS Seal Ring (O-Ring)

Research on aging and working life of material for GIS sealing O-rings

A Three-Factor Accelerated Aging Test Platform of Thermal, Mechanical Compression, Pressured SF 6 , and a Leakage Test System for GIS O-Ring Seals

The Change of Sealing Property in the Aging Process of NBR Sealing Equipment Based on Finite Element Analysis

The effect of aging during storage on the performance of a radial lip seal

Leakage analysis of B shape ring self-energized seal in high pressure polythene polymerizer due to the aging of its nonmetallic ring

The effect of aging in oil on the performance of a radial lip seal

Prediction for O-Ring Type Sealing Ring's Storage Life Based on Accelerated Ageing Data

Multiscale simulation on dynamic friction behavior of cylinder sealing rings under hydrothermal aging

Aging Characteristics and Repairing Evaluation of Long-term Operating LSR Bushings

Compatibility of C5F10O with common-used sealing materials: An experimental study

Study on Aging Evaluation Method of Silicone Rubber in Dongguan

The Influence of Oil and Thermal Aging on the Sealing Characteristics of NBR Seals

Synergistic Effects of Multiple Environmental Factors on Degradation of Silicone Rubber Seals under Marine Atmosphere

Experimental Research on Ageing of Insulation Silicone Oil in Cable Terminal of Gas Insulated Switchgear

Analysis of O-Ring Seal Failure under Static Conditions and Determination of End-of-Lifetime Criterion

Analysis of material fault of O-ring seal in aircraft cylinder

Long-term sealing performance evaluation and service life prediction of O-rings under thermal-mechanical coupling conditions

Research status and prospect of wear and aging on hydraulic rubber sealing materials

Study on the aging of three typical rubber materials under high- and low-temperature cyclic environment