Abstract:The fabrication of AlCo0.2CrFeNi2.1 high entropy alloy via laser metal deposition (LMD) was motivated and implemented by the demand for overcoming the strength-ductility trade-off of the as-cast alloys due to the Co concentration. The microstructure features of AlCo0.2CrFeNi2.1 alloy were characterized by scanning electron microscopy, X-ray diffraction, transmission electron microscopy, and electron back-scattered diffraction. The mechanical properties were evaluated by a tensile test at room temperature. The synergy of reduced Co content and LMD process led to the formation of hierarchical eutectic microstructures consisting of columnar grains, eutectic colonies, alternately arranged fcc(L12)+B2 lamellae, and coherent Cr-rich nanoprecipitates in B2. The growth direction of those eutectic structures was found to be mainly parallel to the building direction (BD). The fcc(L12)/B2 eutectics agreed well with the Kurdjumov–Sachs orientation relationship of {110}B2//{111}L12, and B2// L12. The LMD fabricated AlCo0.2CrFeNi2.1 exhibited anisotropic mechanical properties when stretched in BD and transverse direction (TD). An excellent combination of the ultimate tensile strength (1246 MPa) and ductility (17.1%) was achieved in the BD, better than the as-cast counterpart. The elevated mechanical properties could be attributed to the high cooling rate solidification induced microstructural refinement. The same interlamellar spacing in BD and TD embraced a nearly equal ability to block dislocation movement and gave rise to the similar yield tensile strength. The differences in grain/colony size induced boundary strengthening in BD and TD were evaluated to account for the remarkable changes in ultimate tensile strength as well as ductility.

Growth Morphology of CuMg2 in Laser Forming of AlCoCrCuFeNi Coating on Mg

Solidified characteristic and enhanced properties of Al 0.5 MnFeNiCu 0.5 /Al–Ni functionally gradient coating fabricated by laser cladding on AZ91HP

Laser Cladding Fe/FeCr Coatings on Continuous Casting Cu Mold

Research on the laser melting coating process of an AlCoCrFeNi high‐entropy alloy

Microstructural Transformation and High-Temperature Aluminum Corrosion Properties of Co-Based Alloy Coating Prepared by Laser Cladding

Laser assisted synthesis of Al0.1CoCrFeNi High Entropy Alloy Coating: Microstructures and Properties

Microstructures and properties of AlCrFeNiMnx high-entropy alloy coatings fabricated by laser cladding on a copper substrate

Solidification Behaviour and the Evolution of Microstructure in the Laser Cladding of Aluminium on Magnesium Substrate

Synthesis and characterization of FeCoNiCrCu high-entropy alloy coating by laser cladding

Microstructures and Mechanical Properties of CrMnFeCoNi High Entropy Alloys Fabricated Using Laser Metal Deposition Technique

A novel strategy for promoting corrosion and wear resistance of Mg-Li alloys: Gradient eutectic high-entropy alloy coating induced by in-situ bidirectional diffusion

Hierarchical eutectic structure and superior mechanical property in low cobalt content AlCo0.2CrFeNi2.1 alloy by laser metal deposition

Heat Treatment-Induced Microstructure and Property Evolution of Mg/Al Intermetallic Compound Coatings Prepared by Al Electrodeposition on Mg Alloy from Molten Salt Electrolytes

Preparation of CrCoFeNiMn High-Entropy Alloy Coatings Using Gas Atomization and Laser Cladding: An Investigation of Microstructure, Mechanical Properties, and Wear Resistance

Wear and Corrosion Resistance of Al0.5CoCrCuFeNi High-Entropy Alloy Coating Deposited on AZ91D Magnesium Alloy by Laser Cladding

Manufacturing of FeCoCrNiCux Medium-Entropy Alloy Coating Using Laser Cladding Technology

Investigation on the Two-Stage Hierarchical Phase Separation in the Laser Cladded Cu–Mn–Fe Coating

Influences of Heat Input on the Geometric Parameters and Element Distribution of CrMnFeCoNi High-Entropy Alloy Coating on Aluminum Alloy Using Laser Cladding

A novel laser-cladded AlCuTiVCr/Cu-Al functionally graded coating with excellent corrosion resistance on Mg-Li alloy

Investigation of the Microstructure and Properties of CoCrFeNiMo High-Entropy Alloy Coating Prepared through High-Speed Laser Cladding