Validation of Creep Crack Growth NSW Model in Extrapolating Short-Term Laboratory Test Results to Longer-Term Service Component Failure Prediction

Shervin Maleki,Yan-Hui Zhang,Kamran Nikbin

2011-01-01

Abstract:Due to technical and financial restrictions in test duration the extrapolation of short-term laboratory test results to predict long-term high temperature service component failure, has always been an area of concern when conducting a fitness for service or remaining life assessment. The P91 material is of particular concern due to the complication of phase transformation in long service duration as well as its tendency to type IV cracking. The current NSW model is shown to be capable of predicting upper/lower bounds of creep crack growth in a range of steels when data are obtained from relatively short to medium-term laboratory experiments (< 10,000 hours). However more recent literature presenting uniaxial creep and crack growth tests indicates that some materials show relatively brittle behaviour and smaller failure strain during longer term laboratory tests. This may be predicted by NSW model using short term uniaxial data. This paper compares and analyses the response of the current NSW model to predict the creep crack propagation rate in the relatively low C* regime (<10(-5)) based on the available test data on modified 9Cr material.