Low-Cycle Fatigue Behaviors of Small Cracks of Glidcop Al-15

Y. Yin,H. B. Chen,W. L. Xiao
2011-01-01
Abstract:Glidcop Al-15, a dispersion strengthened copper alloy containing 0.15% of submicroscopic alumina particles, is a particularly attractive material for high temperature components because of its excellent thermal conductivity, strength retention and micro-structural stability at elevated temperatures [1-3] As fatigue damage requires to be expressed in terms of a crack, observations are made on Glidcop Al-15 that relate to the initiation zones and the propagation of small cracks subjected to low cycle fatigue and these observations are based on surface replica studies [4, 5]. On the other hand, the effect of prior fatigue history on the growth rate of a small crack is investigated systematically using special specimens containing an artificial small hole of various diameters, i.e. 40, 100 and 200 pm at three different load levels equivalent to cyclic stress levels separately. Similar experiments for a medium carbon steel NO.45 are also operated for comparison with the results of Glidcop Al-15 [6].Hour-glass shaped specimens which have a minimum diameter of 8 mm at the central cross-section are used in the fatigue tests. These specimens are called 'plain specimens'. To simulate a defect or an inclusion, a very small hole was drilled on the periphery of the central portion of a plain specimen. The diameter d of the hole and its depth were identical, as indicated in Figure 1. Three hole diameters were used, with d equal to 40, 100 or 200 mu m. These specimens are called 'holed specimens'.[GRAPHICS]Push pull low-cycle fatigue tests were carried out on a material-testing machine that kept the cyclic stress amplitude constant. The test frequency depended on the particular stress strain range. A lower test frequency was used at the higher strain ranges in order to avoid heating in the specimen.Test results indicate that the log log relation between the cyclic plastic strain range and the number of stress cycles to failure of all the specimens, including the medium carbon steel NO.45 and Glidcop Al-15 of both plain and holed specimens, are linear for the Coffin-Manson type and the fatigue life decreases with an increase in the hole diameter d for both two materials. On the other hand, slopes of the log log relations of each specimen type are similar for the same material, which is indicative of the same fatigue process being operated in all specimens, irrespective of the applied cyclic stress strain level. Besides the experiments show a trend that the dimensionless fatigue life N-f/N-f0 becomes longer with decreasing d while N-f0 is the fatigue failure life of plain specimens and N-f is the one of holed specimens. In the case of the specimen with the smallest hole diameter (d=40 mu m), the fatigue life is about the same as that of plain specimens. Through the experiments, it is observed that the total life of specimens is dominated by crack propagation. The crack initiation site in holed specimens is always at either the surface edge or the root of the hole. After all, prior fatigue history shows little influence on the crack growth rate in the high-strain fatigue regime.These experiments can provide the fundamental experiment data for further predicting the fatigue life of Glidcop Al-15.
What problem does this paper attempt to address?