Abstract:Carbon fiber-reinforced polymers (CFRP) have been actively employed as lightweight materials; yet, evaluating the material’s reliability under multi-axis stress states is still challenging owing to their anisotropic nature. This paper investigates the fatigue failures of short carbon-fiber reinforced polyamide-6 (PA6-CF) and polypropylene (PP-CF) by analyzing the anisotropic behavior induced by the fiber orientation. The static and fatigue experiment and numerical analysis results of a one-way coupled injection molding structure have been obtained to develop the fatigue life prediction methodology. The maximum deviation between the experimental and calculated tensile results is 3.16%, indicating the accuracy of the numerical analysis model. The obtained data were utilized to develop the semi-empirical model based on the energy function, consisting of stress, strain, and triaxiality terms. Fiber breakage and matrix cracking occurred simultaneously during the fatigue fracture of PA6-CF. The PP-CF fiber was pulled out after matrix cracking due to weak interfacial bonding between the matrix and fiber. The reliability of the proposed model has been confirmed with high correlation coefficients of 98.1% and 97.9% for PA6-CF and PP-CF, respectively. In addition, the prediction percentage errors of the verification set for each material were 38.6% and 14.5%, respectively. Although the results of the verification specimen collected directly from the cross-member were included, the percentage error of PA6-CF was still relatively low at 38.6%. In conclusion, the developed model can predict the fatigue life of CFRPs, considering anisotropy and multi-axial stress states.

Probabilistic Modeling of Stiffness Degradation for Fiber Reinforced Polymer under Fatigue Loading

Probabilistic Fatigue Stiffness Degradation of Frp Laminates Considering Stress Ratio Effects

Probabilistic Fatigue Stiffness Variation of Angle-Ply GFRP Composites Considering Stress Ratio Effect

A Model of Strength Degradation for Glass Fiber Reinforced Polymer Composite Laminates under Fatigue Loading

Strength and stiffness degradation modeling and fatigue life prediction of composite materials based on a unified fatigue damage model

A Fatigue Damage Model for FRP Composite Laminate Systems Based on Stiffness Reduction

Fatigue Reliability Analysis of Composite Material Considering the Growth of Effective Stress and Critical Stiffness

A Fatigue Residual Strength Model for Composite Laminates Based on Residual Stiffness Ratio

A Nonlinear Fatigue Damage Model for Life Prediction of Composite Laminates

Novel Mathematical-Statistical Models for the Distribution of Fatigue Life and Residual Strength for Fiber Reinforced Polymer Composites

A New Probability Model of Residual Strength of Material Based on Interference Theory

A New Approach to Fatigue Damage Modeling of Composite Laminates

A Methodology to Predict the Fatigue Life under Multi-Axial Loading of Carbon Fiber-Reinforced Polymer Composites Considering Anisotropic Mechanical Behavior

A Full-Range Fatigue Life Prediction Model for RC Beams Strengthened with Prestressed CFRP Plates Accounting for the Impact of FRP Debonding

Prediction of the Fatigue Life Based on Stiffness Degradation Concept

A Fatigue Model to Predict Interlaminar Damage of FRP Composite Laminates Subjected to Mode I Load

Experimental and Analytical Study on Residual Stiffness/Strength of CFRP Tendons under Cyclic Loading

A Novel Method for Failure Probability Prediction of Plain Weave Composites Considering Loading Randomness and Dispersion of Strength

An Investigation on Residual Strength and Failure Probability Prediction for Plain Weave Composite under Random Fatigue Loading

TEMPERATURE EFFECT ON FATIGUE PERFORMANCE OF FIBER-REINFORCED POLYMER

A Damage Mechanics Model for Fatigue Life Prediction of Fiber Reinforced Polymer Composite Lamina