Strength, Ductility and Fracture Strain of Press-Hardening Steels

Yi Hongliang,Chang Zhiyuan,Cai Helong,Du Pengju,Yang Dapeng

DOI: https://doi.org/10.11900/0412.1961.2020.00003

IF: 1.797

2020-01-01

ACTA METALLURGICA SINICA

Abstract:Press-hardening steels (PHS) are increasingly used for vehicle body structure components because of their lightening potential owning to superiorly high strength, adequate ductility and fracture resistance. New PHS grades with higher strength and enhanced fracture resistance are being widely studied now for achieving further vehicle weight reduction, and the recent development in this field is reviewed in this article. Combining quenching and partitioning (Q&P) with the hot stamping process has been explored by some researchers, as well as tempering after the hot stamping using the medium-Mn steels. A certain amount of austenite could remain by the above processes and the resulted tensile strength can exceed 1500 MPa while tensile ductility of 10%-16% can be achieved utilizing the transformation-induced plasticity (TRIP) effect. A V micro-alloyed steel (34MnB5V) for hot stamping has been designed, utilizing both grain refinement and precipitation strengthening of VC. The tensile strength of the newly developed 34MnB5V exceeds 2000 MPa which is much higher than that of the most commonly used PHS 22MnB5 (1500 MPa). Meanwhile, the ductility and bending properties of the above two steels are comparable. Al-Si coated PHS is usually adopted to avoid oxidation during heating and improve its corrosion resistance after stamping. However, its bendability after forming is lower than that of the bare grade when surface decarburization is absent. The thickness of the brittle FeAl, phase was reduced and the carbon enrichment at the interface of a-Fe and martensite matrix was weakened after hot stamping by thinning of the Al-Si coating. Thus, the bending property was improved. The applicability of the new designed processes for the existing production lines should be considered in future studies. The bending test should be adopted for the deformability evaluation rather than the uniaxial tensile test simply. The welding property and the mechanism of hydrogen embrittlement should also be studied for industrial application of the new developed steels.