Rapid Solidification of Ti-6Al-4V Alloy Micro-Droplets Under Free Fall Condition

ZHAI Bin,ZHOU Kai,Lü Peng,WANG Haipeng

DOI: https://doi.org/10.11900/0412.1961.2017.00312

IF: 1.797

2018-01-01

ACTA METALLURGICA SINICA

Abstract:Especially in the past decades, Ti-6Al-4V alloy has received much attention, not only due to its high melting temperature, good corrosion resistance, low density and high hardness, but also because of the diverse and complicated microstructures formed under different conditions. This makes Ti-6Al-4V a potential candidate in both aerospace industries and fundamental research. It is well known that the solidified microstructures of alloy have a great influence on their mechanical properties. Therefore, it is crucial to investigate the mechanical properties of Ti-6Al-4V solidified under different conditions, in particular in the undercooling conditions. However, it is noted that most research on the solidification of Ti-6Al-4V alloy was carried out under equilibrium condition. With respect to Ti-6Al-4V alloy solidified under substantial undercooling conditions, few studies could be found. Thus, it is interesting to study two points: (1) the feature of the microstructure of Ti-6Al-4V alloy solidified under highly undercooled conditions and large cooling rate, (2) the influence of undercooling and cooling rate on the mechanical property of Ti-6Al-4V alloy. To address these two problems, Ti-6Al-4V alloy was rapidly solidified in a drop tube. The main results are summarized as follows. The microstructure of the Ti-6Al-4V alloy solidified under free fall condition displays "lamellar a+b→adendrites→basket-weave a'+b→needle-like a'→needle-like a'+anomalous b" transfor mation with decreasing the droplets diameter. And the needle-like a' phase in the original boundaries of equiaxed bgrains is transformed into a continuous distribution and anomalous structure of bphase when the droplet size is less than about 400 mm. The microhardness of this alloy ranges from 506 kg/mm2to 785 kg/mm2when the droplet diameter decreases from 1420 mm to 88 mm, which is much higher than that of the master alloy. For "lamellar structure of a+bphases", "needle-like a'phase" and "needle-like a' phase+anomalous bphase", the microhardness increases with the decrease of droplet diameter. But for 'basket-weave' microstructure, the microhardness diminishes with the decrease of droplet diameter.