Study On. Electrochemical Copolymerization of Aniline with P-Phenylenediamine on Ito Electrode by in Situ Uv-Vis Spectroscopy and Characterization of the Copolymer

Gui-Rong Zhang,Cheng-Tian Xu,Ai-Jian Zhang,Li Chen,Jia-Xing Lu
DOI: https://doi.org/10.3321/j.issn:0567-7351.2008.03.014
2008-01-01
Acta Chimica Sinica
Abstract:It was observed by in situ UV-Vis spectrometry that the polymerization of p-phenylenediamine and the electrocopolymerization between aniline and p-phenylenediamine. happened by cyclic voltammetry in a 0.5 mol/L sulfuric acid media, and that the polymerization reactions became faster due to the addition of p-phenylenediamine. Experimental results showed that the absorbance band at 430 nm in in situ UV-Vis spectra disappeared because of the presence of p-phenylenediamine. The reason leading to these results might be that the cation radical intermediate produced from aniline reacted with the p-phenylenediamine cation radical during polymerization. It was a direct evidence which indicated that the addition of p-phenylenediamine changed the mechanism of the electro-polymerization of aniline on an ITO electrode in a 0.5 mol/L sulfuric acid solution. The reflectance FTIR spectra of films deposited on the ITO electrode was obtained, which showed that p-phenylenediamine could be incorporated into the copolymer films by 1,2- or 1,2,3-substituted modes. The SEM images of the films showed that the additional p-phenylenediamine could change markedly morphology of the films and promoted the growth of fibrous morphology with a large area. The diameter of the fiber in the film grown on the ITO electrode might reach 50 urn. The electrochromic behavior of the polymer films was studied in detail. At the potential ranged from 0.0 to 0.6 V, the in situ UV-Vis spectra of the copolymer film deposited on the ITO electrode was obviously different from that of polyaniline film on the ITO electrode. The electrochromic reversibility of the copolymer was better than that of polyaniline. Furthermore, SEM morphology images indicated that electrolyzing polyaniline and copolymer on the ITO electrode at 0.8 V in the 0.5 mol/L H2SO4 made them aggregate.
What problem does this paper attempt to address?