Abstract:Phase pure and clean MgB2 films have been fabricated on different types of single-crystal substrate, including SiC, sapphire, MgO, LaAlO3, SrTiO3, and yttrium-stabilized ZrO2 (YSZ), via the hybrid physical-chemical vapor deposition (HPCVD) technique. Pure MgB2 films with different structural textures are obtained by selecting the substrate and its orientation, such as off-axis epitaxial MgB2 on MgO(211) or textured MgB2 on YSZ(110) substrates. Films show T-c(0) in the range 37-41 K, and residual resistivity rho(42 K) between 0.3 and 5 mu Omega cm as the substrate and film thickness are varied. The crystal structures and film morphologies are presented and discussed. Further investigations are focused on c-axis epitaxial films. Epitaxial MgB2 films with thickness about 300 nm manifest T-c(0) = 41.2 K and residual resistivity .(42 K) = 0.35 mu Omega cm on SiC(0001) while T-c(0) = 39.5 K and rho(42 K) = 0.27 mu Omega cm on c-cut sapphire, reflecting that the films are of high quality and in the 'clean limit'. Low upper critical field H-c2(parallel to ab)(0) and large anisotropy of the upper critical field gamma comparable to the results from MgB2 single crystals are also revealed. The smooth surface of the epitaxial films, with root-mean-square (RMS) roughness less than 5 nm, makes them well qualified for device applications. Microwave performance measurements are carried out using a coplanar resonator on a 300 nm thick film on sapphire substrate and no power dependence of unloaded quality factor in the output power range of -10-25 dB is found.

Study on single crystal MgB2 nanosheets grown by hybrid physical-chemical vapor deposition

Aligned single crystal MgB<sub>2</sub> nanowires

Single-crystal MgB2 Hexagonal Microprisms Via Hybrid Physical-Chemical Vapor Deposition

Potential Enhancement of Superconductivity in MgB2 Nanosheets: First-principles Calculations

Hybrid Physical-Chemical Vapor Deposition of Ultrathin Mgb2 Films on Mgo Substrate with High T-C and J(C)

Biaxial Strain Engineering on the Superconducting Properties of MgB2 Monolayer

Growth of MgB2 Thin Film Fabricated on Mg Substrate by Hybrid Physical-Chemical Vapor Deposition

MgB2 Superconducting Whiskers Synthesized by Using the Hybrid Physical-Chemical Vapor Deposition.

Synthesis of Boron and Boride Compounds Nanowire Arrays by Chemical Vapor Deposition

Thick MgB2 film with (101) oriented micro-crystals

Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder

GROWTH AND PROPERTIES OF SUPERCONDUCTING MgB_2 THIN FILM FABRICATED ON Al_2O_3 SUBSTRATE BY HYBRID PHYSICAL CHEMICAL VAPOR DEPOSITION

A novel two-dimensional MgB6 crystal: metal-layer stabilized boron kagome lattice

In Situ Epitaxial MgB2 Thin Films for Superconducting Electronics

Clean Mgb2 Thin Films On Different Types Single-Crystal Substrate Fabricated By Hybrid Physical-Chemical Vapor Deposition

Superconducting Mgb2 Thin Films On Silicon Carbide Substrates By Hybrid Physical-Chemical Vapor Deposition

Thermochemical analysis of MgB2 synthesis by molecular-beam epitaxy

MgB2 thick film with TC = 40.2 K deposited on sapphire substrate

MgB<sub>2</sub> Thick Film Grown on Silicon Carbide Substrate by Hybrid Physical-Chemical Vapor Deposition

Review of superconducting properties of MgB2

Anisotropy of superconductivity of as-grown MgB$_2$ thin films by molecular beam epitaxy