Effect of P-complex on 3,4-Structure of Polyisoprene during Anionic Polymerization

Tian-yi Li,Bo Chen,Shang-han Wu,Min-ze Shu,Yong Guan,An-na Zheng

2014-01-01

Acta Polymerica Sinica

Abstract:Polyisoprene (PI) with high 3,4-structure content (78.76%) was synthesized by anionic polymerization using n-BuLi as the initiator and tetrahydrofuran/cyclohexane as the mixed solvent. P-complex was also introduced into the system to improve the controllability of the polymerization. The molecular structure was characterized by H-1-NMR. Results indicated that when n-BuLi was used as the initiator,the polymerization rate and molecular structure of the products were determined by the channel space between the ion pairs. When the channel space was compatible with the requirement for inserting of the monomers, the polymerization rate would be maximum. The channel space required for 3,4 polymerization of isoprene is the smallest. P-complex with same lithium atom as initiator and large steric hindrance can adjust the channel space between the cation-anion pairs. P-complex can partially block the channel space. Therefore, the introduction of a small dosage of P-complex could not only accelerate 3,4 polymerization, inhibit 1,2 and 1,4 polymerization effectively, but also increase the content of 3, 4-PI. On the contrary, with the increase of the temperature, the channel space expanded, resulting in the decrease of 3, 4-PI content and the increase of 1, 4-PI content. The higher the temperature was,the more content of trans-1,4-PI would be.