Synthesis of polyisoprene catalysized by molybdenum catalyst system

Tian Yumin,Cao Kun,Hua Jing,Xu Ling

DOI: https://doi.org/10.3969/j.issn.1000-1255.2011.01.009

2011-01-01

Abstract:Isoprene was polymerized with main catalyst MoCl5(simplified as Mo) modified by solubilizers and co-catalyst Al(OPhCH3)(i-Bu)2(simplified as Al).The effects of three different solubilizers of octanol,tributyl phosphate(TBP) and(TBP+octanol) on catalytic activity and polymer′s intrinsic viscosity were studied,the effects of the Al/Mo(mole ratio),Al/isoprene(Ip)(mole ratio) and the polymerization time on monomer conversion and polymer′s intrinsic viscosity were investigated in the MoCl3(OC8H17)2-Al(OPhCH3)(i-Bu)2 catalyst system,the relative molecular mass and its distribution were measured,and the microstructure of polymer was characterized.The results showed that the octanol could greatly improve the catalytic activity and the intrinsic viscosity ranged from 0.6 dL/g to 1.7 dL/g.The catalyst exhibited higher activity when Al/Mo was 8,both of the catalytic activity and polymer′s intrinsic viscosity increased at first and then decreased with the increase of Al/Mo.With increasing the Mo/Ip,the Ip conversion raised and achieved 80% at Mo/Ip of 3×10-3,but the intrinsic viscosity had a inverse relationship with Mo/Ip.The conversion increased with polymerization time and got stable after 30 h.However,the intrinsic viscosity reached the maximum of 2 dL/g at 5 h and then decreased.The gel permeation chromatography trace exhibited a relatively narrow unimodal molecular weight distribution.The mole fraction of 1,2-unit and 3,4-unit was about 72%.