Abstract:Fe3O4@SiO2 particles were synthesized by a solvothermal method and a classical stOber method. Superparamagnetic Fe3O4 was the core, and a sol-gel coating of SiO2 was the shell. After the SiO2 surface was modified with amino groups, benzaldehyde was conjugated to the particles by a Schiff base reaction. The Fe3O4@SiO2 particles were emulsified in paraffin/water as a solid emulsifier to obtain an oil-in-water Pickering emulsion. After cooling the paraffin, the particles were fixed on the surface of the emulsion droplets. The particles were etched in ammonium fluoride aqueous solution, and Janus particles with different structures could be obtained by adjusting the etching time. Via the in situ growth of metal Pt or Ag nanoparticles, superparamagnetic Fe3O4@SiO2-Pt or Fe3O4@SiO2-Ag Janus particles were obtained. The movement of Fe3O4@SiO2-Pt Janus particles was observed due to the catalytic decomposition of hydrogen peroxide aqueous solution. It was found that in the short term, there was a linear motion, while in the long term, the motion direction and trajectory were random. Fe3O4@SiO2-Ag Janus particles were used as magnetic solid surfactants to stabilize the emulsions and catalyze the nitro reduction. About 60% of the surficial area of the Janus particles was modified by phenyl groups, while the remaining 40% was covered with Ag nanoparticles. Under the premise of maintaining the Janus balance, the whole particle became more hydrophobic, which was conducive to the formation of the water-in-oil emulsion. In addition, the Ag side of the Janus particles was towards the aqueous phase, and the opposite hydrophobic side was towards the oil phase. The Janus particles possessed a fixed orientation assembly at the oil-water interface. The assemble membrane possessed Janus characteristics, and it facilitated the stable dispersion of the emulsion and the catalysis. The method has the advantages of a simple principle, capability for mass production, universality and versatility. It is expected that Janus particles will be used to more precisely regulate the zoning with different functional substances.

Single Polymer Chain Grafted Fe3O4 Composite Janus Nanoparticle

Polymer-Fe3o4 Composite Janus Nanoparticles

Fumed Silica/polymer Hybrid Nanoparticles Prepared by Redox-Initiated Graft Polymerization in Emulsions

Responsive Single-Chain/Colloid Composite Janus Nanoparticle

Emulsion Interfacial Synthesis of Polymer/Inorganic Janus Particles

Preparation of Polymer-Based Nano-Assembled Particles with Fe3O4 in the Core

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Single-Chain Janus Nanoparticle by Metallic Complexation

Synthesis of PPEGMEA-g-PMAA Densely Grafted Double Hydrophilic Copolymer and Its Use As a Template for the Preparation of Size-Controlled Superparamagnetic Fe3O4/polymer Nano-Composites

Multifunctional Fe3O4@SiO2 Janus Particles

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Large-Scale Synthesis of Reactive Janus Inorganic/Polymer Colloidal Dimer

Janus Composite Nanorod from a Molecular Bottlebrush Containing a Block Copolymer.

Janus Nanosheets of Polymer-Inorganic Layered Composites

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Polymer/Metal Segmental Janus Nanoparticles

The Stepwise Organization of Nanoparticles into a Pickering Emulsion.

Responsive Janus Composite Nanosheets

Diblock Copolymer Based Janus Nanoparticles

Spatial Isolation of Carbon and Silica in a Single Janus Mesoporous Nanoparticle with Tunable Amphiphilicity

Bottlebrush Colloid Janus Nanoparticles