Studies on Multilayer Microstructure of Nanosilica Filled Carboxylated Styrene-Butadiene Rubber

Rui-quan Yang,Yi-hu Song,Qiang Zheng

DOI: https://doi.org/10.11777/j.issn1000-3304.2016.16025

2016-01-01

Acta Polymerica Sinica

Abstract:Carboxylated styrene-butadiene rubber/nanosilica (XSBR/A200) composites with an extraodinarily wide range of A200 loading (0 - 300 phr) were prepared by absorption mixing. The composites with 0 - 60 phr of A200 were also been fabricated by latex mixing plus extra open-milling methods. Temperature modulated differential scanning calorimetry (TMDSC) was used to investigate glass-transition behavior of composites prepared by both methods, while dynamic rheology tests were carried out to investigate the reinforcement of the compounds prepared by the latex mixing plus extra open-milling methods. TMDSC results show that the content of the glassy layer immobilized in the close vicinity of A200 nanoparticles increases proportionally with silica loading regardless of mixing methods. Comparision between TMDSC and rheology results indicates that there exists an outer absorption layer besides the glassy layer in compounds. The glassy layer corresponds to the XBSR fraction surrounding nanosilica that does not undergo glass transtion. On the other hand, the outer layer is able to undergo glass transition together with the bulky rubber phase but it behaves rigidly at high frequencies. These two layers contribute both to the reinforcement effect. Assuming equivalent A200 spheres of 6.8 nm in radius, equivalent thicknesses of the glassy and outer layers are estimated as 1.0 nm and 1.6 nm, respectively.