Syndiotactic Homo- and Co-polymerization of &ITp&IT-Fluorostyrene and Ethylene Catalyzed by Half-sandwich Scandium Complexes

Na Jiao,Fang Guo,Yang Li
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17051
2017-01-01
Acta Polymerica Sinica
Abstract:Syndiotactic polymerization of p-fluorostyrene and its copolymerization with ethylene catalyzed by half-sandwich scandium complex (C5Me4SiMe3)Sc(CH2C6H4NMe2-o)(2) (1) and (C5Me4 SiMe3)Sc(CH2SiMe3)(2) (THF) (2) have been examined. The microstructures and thermal properties of the obtained polymers were characterized by H-1-NMR, C-13-NMR, GPC and DSC. Scandium complex 1 showed syndiotactic selectivity for the polymerization of p-fluorostyrene with low activity (10(3) g polymer mol(sc)(-1) h(-1)). Scandium complex 2 proved to be a high activity catalyst for the polymerization of p-fluorostyrene to afford syndiotactic or atactic poly(p-fluorostyrene) by controlling the type and the volume of the solvent. When the concentration of p-fluorostyrene in chlorobenzene was below 2.4 mol/L, the syndiotactic poly(p-fluorostyrene) (rrrr > 99%) was obtained with scandium complex 2 possessing high activity (10(5)g polymer mol(sc)(-1) h(-1)). The melting point (T-m) of syndiotactic poly(p-fluorostyrene) reached up to 324 degrees C, suggesting the semicrystalline morphology of this polymer. The molecular weight of the syndiotactic polyp-fluorostyrene) (M-n = 3.10 x 10 (4) - 2.08 x 10(5)) was easily controlled by changing the feed ratio of p-fluorostyrene to catalyst. When the concentration of p-fluorostyrene in chlorobenzene was above 4.8 mol/L or fluorobenzene used as solvent, atactic polyp-fluorostyrene) with controllable molecular weight (3.80 x 10(4) - 1.88 x 10(5)) was obtained. Moreover, the copolymerizations of p-fluorostyrene with ethylene catalyzed by complexes 1 or 2 have also been prepared, leading to novel copolymers with controlled composition (p-fluorostyrene content: 41 mol% - 88 mol%) and molecular weight (3.10 x 10(4) - 1.84 x 10(5)), and with high activity (up to 10(6) g polymer mol(sc)(-1)h(-1)). When ethylene content in the copolymer is higher than that of p-fluorostyrene, the copolymers showed a T-m around 119 - 126 degrees C owing to polyethylene blocks. When p-fluorostyrene content in the copolymer is higher than that of ethylene, the obtained copolymers with syndiotactic poly(p-fluorostyrene) blocks, prepared by scandium complex 1, showed a T-m around 269 - 282 degrees C and a T-g around 79 - 82 degrees C; In contrast, the copolymers with atactic poly(p-fluorostyrene) blocks prepared by scandium complex 2 showed their T-g around 94 - 96 degrees C.
What problem does this paper attempt to address?