Abstract:With inspiration from the structure of macromolecular thioether generated in the 9H-xanthene-9-thione mediated radical polymerization, five thioethers containing 9-alkyl-9-phenylthio/methylthio-xanthene structure were synthesized. Xanthydrol was selected as the precursor for two 9-substituted xanthene intermediates. 9-(Phenylthio)-9H-xanthene was obtained via a condensation reaction between xanthydrol and thiophenol in the presence of perchloric acid as catalyst. 9-(Methylthio)-9H-xanthene was obtained via the thioetherification of the chlorinated product of xanthydrol with sodium methyl mercaptide. The sulfurated intermediates were deprotonated by n-butyl lithium, and transformed into five target products via substitution reactions with three alkyl halides individually. H-1-NMR, C-13-NMR, FTIR and UV-Vis analyses were conducted to confirm and characterize the thioethers. Afterwards, a systematic study on the polymerization behavior of styrene (St) initiated by the thioethers was carried out in the absence and presence of a thermal initiator. Bulk polymerizations of St were initiated successfully by the thioethers at 80 degrees C with relatively low monomer conversions, and the reactions exhibited uncontrolled polymerization behaviors without obvious increase in number-average molecular weight (M-n) in the polymerization process with the PDI of polymeric products above 3.0. However, when the thioethers were used together with 2,2'-azobis(2,4-dimethyl) valeronitrile (ABVN) in the solution polymerization of St in toluene at 65 degrees C, higher monomer conversions compared with those of bulk polymerization and certain controllability could be achieved, reflected by a linear increase in M-n with conversion. Besides, the effects of molar ratio of ABVN to thioether and reaction temperature on the polymerization behavior of St were investigated in detail. A reduction in the molar ratio of ABVN to thioether would cause a reduction in the concentration of propagating radicals, and lead to a decrease in monomer conversion. But the PDI of polymeric product narrowed down indicating a controllable polymerization. Furthermore, elevated reaction temperature brought about an increased concentration of chain radical, and resulted in a relatively low M-n with a broadened PDI.

Synthesis and Characterization of Trifluoromethyl Substituted Styrene Polymers and Copolymers with Methacrylates: Effects of Trifluoromethyl Substituent on Styrene

Synthesis and properties of copolymers of methyl methacrylate with 2,3,4,5,6‐pentafluoro and 4‐trifluoromethyl 2,3,5,6‐tetrafluoro styrenes: An intrachain interaction between methyl ester and fluoro aromatic moieties

2,2‐Bistrifluoromethyl‐4,5‐difluoro‐1,3‐dioxole‐co‐tetrafluoroethylene Copolymers with Different Compositions: Synthesis, Chain and Condensed Matter Structures and Optical Properties

Alkyl Halide/tertiary Amine As Novel Initiators for Free Radical Polymerizations of Methyl Methacrylate, Methyl Acrylate and Styrene

Syndiospecific styrene polymerization with CpTiCl3/MAO: Effects of the order of reactant addition on polymerization and polymer properties

Copolymers of methyl methacrylate with N‐trifluorophenyl maleimides: High glass transition temperature and low birefringence polymers

Nitroxide-Mediated Controlled Radical Copolymerization of Î±-Trifluoromethylstyrenes with Styrenes

Copolymers of 2,5‐bis[(4‐methoxyphenyl) Oxycarbonyl]styrene with Styrene and Methyl Methacrylate: Synthesis, Monomer Reactivity Ratios, Thermal Properties, and Liquid Crystalline Behavior

Isospecific Polymerization of Halide- and Amino-Substituted Styrenes Using a Bis(phenolate) Titanium Catalyst

Thermal and Optical Properties, and Aggregated Structure of Poly(substituted methylene)s Produced by Radical Polymerization of Fumarates Containing Fluorine-Substituted Alkyl Ester Groups

Synthesis and characterization of a thermotropic liquid-crystalline poly[2,5-bis(4′-alkoxycarbonylphenyl) styrene]

A Novel Perfluorocyclobutyl Aryl Ether-Based Graft Copolymer Via 2-Methyl-1,4-bistrifluorovinyloxybenzene and Styrene

Synthesis and Characterization of Copolymer of 2,5-Bis[(4-methoxyphenyl)oxycarbonyl]styrene and Styrene with High Molecular Weight

Synthesis and Characterization of Poly[styrene‐b‐methyl(3,3,3‐trifluoropropyl)siloxane] Diblock Copolymers Via Anionic Polymerization

Synthesis and Properties of Styrene-N-Phenylmaleimide-Maleic Anhydride Tercopolymer

Synthesis and Characterization of Poly[4‐(2‐thiazolylazo)phenyl Methacrylate]‐co‐poly(methyl Methacrylate)

Preparation of a Novel Styrene Copolymer: Simultaneously Improving the Thermal Stability and Toughness

STUDIES ON THE MODIFICATIONS OF SULFUR CONTAINING OPTICAL PLASTICS BY COPOLYMERIZATION WITH STYRENE

Synthesis of Thioether Compounds and Their Application in Initiating/Controlling the Radical Polymerization of Styrene

Synthesis and Characterization of Polystyrene-G-polydimethylsiloxane Copolymers

Copolymerization of Α-Methylstyrene and Styrene