Preparation of Thermo-Sensitive Polymer Microgels by Altered-Temperature Suspension Polymerization

Y Zhang,JD Ding

DOI: https://doi.org/10.3321/j.issn:1000-3304.2005.06.022

2005-01-01

Acta Polymerica Sinica

Abstract:An altered-temperature inverse suspension polymerization, which was suitable for negatively thermosensitive macromers, was presented to prepare thermosensitive and biodegradable microgels. The thermosensitivity and biodegradability of microgels come from those of macromers. The microgels were synthesized in suspension, in which the continuous phase was heptane. Ammonium persulphate and N,N,N',N'-tetramethylethylenediamine were employed as the initiating system. The negatively thermosensitive macromer aqueous solution was first dispersed well at low temperatures (lower than the sol-gel transition temperature of the macromer solution) and then crosslinked after raising temperature. The highlight of this approach is the avoidance of dispersion difficulty of the dispersion phase because of its physical gelation at polymerizing temperature. The thermosensitivity and biodegradation of the resulting microgels were confirmed The volume phase transition temperature of microgels was around 25 degrees C, and the volume of microgels at 37 degrees C was less than half of that at 4 degrees C. Microgels were completely degraded into water-soluble products. It was necessary to add aqueous solutions of initiator and accelerator into the continuous phase after raising temperature. The ratio of oil to water, influenced the morphology of microgels to a certain degree.