Abstract:Using triethylaluminum (TEA), triisobutylaluminum (TIBA) or TEA/TIBA mixtures of molar ratio 75/25, 50/50 and 25/75 as the cocatalyst, five different ethylene–propylene copolymer samples were synthesized by a MgCl2/SiO2/TiCl4/diester type Ziegler–Natta catalyst in a slurry polymerization process. The synthesized copolymers are strongly heterogeneous in chain structure and were fractionated into part of nearly random copolymer and part of segmented copolymer. Both polymerization activity and copolymer structure were found to be markedly changed when the cocatalyst was changed from TEA to TEA/TIBA mixtures or pure TIBA. As the content of TEA in cocatalyst increases, yield of the random part of product increases and the yield of the crystalline segmented copolymer part decreases. There is also a decrease in ethylene content of the whole product with increasing TEA amount. Copolymerization behaviors of the TEA/TIBA mixture activated catalysis systems are not simple superposition of those activated by pure TEA and TIBA. When a 50/50 TEA/TIBA mixture was used as cocatalyst, the copolymerization activity became the highest, and yields of both the random copolymer part and the segmented copolymer part are close to the highest level. On the other hand, both parts of the copolymer produced with a 50/50 TEA/TIBA mixture are relatively more blocky than the products of TEA or TIBA systems, and difference in ethylene content between the random part and the segmented part was the smallest. The segmented copolymer part of three typical samples was further fractionated by temperature-gradient extraction fractionation into fractions of different ethylene content and sequence distribution. Changing TEA content in the cocatalyst exerted strong influences also on the fraction distribution of the segmented part of copolymer.

Influence of Cocatalyst on the Copolymerization of Ethylene and Styrene Catalyzed by N-Catalyst

Polymerization of Styrene Catalyzed by ((PNP)-N-Lambda-P-Lambda) Cobalt(II) Complexes/Ethylaluminum Sesquichloride

Stereospecific Polymerization of 1,3-Butadiene Catalyzed by [NNO] Cobalt Complexes

Stereospecific Polymerization of 1,3-Butadiene Catalyzed by Cobalt Complexes Bearing N-containing Diphosphine PNP Ligands

Polymerization of 1,3-Butadiene Catalyzed by Ion-Pair Cobalt Complexes with (benzimidazolyl)pyridine Alcohol Ligands

Studies on Alternating Copolymerization of Ethylene and Carbon Monoxide Using Nickel‐Based Catalyst: Cocatalyst and the Polarity of Solvent

Polymerization of 1,3-butadiene catalyzed by cobalt(II) and nickel(II) complexes bearing imino- or amino-pyridyl alcohol ligands in combination with ethylaluminum sesquichloride

Ethylene polymerization with metallocene/late transition metal combined catalysts

Effect of Catalysts Supporting on Tandem Polymerization of Ethylene Stock in Synthesis of Ethylene-1-Hexene Copolymer

ETHYLENE POLYMERIZATION WITH CORE-SHELL ZIEGLER-NATTA HYBRID CATALYSTS

ETHYLENE POLYMERIZATIONS CATALYZED BY Α-Diimine COMPLEXES WITH DIFFERENT SUBSTITUENTS ON LIGAND BACKBONE

Highly active Ziegler-Natta Catalysts for propylene polymerization (2) effects of Al/Ti ratio and polymerization temperature

Influence of Cocatalyst on High Temperature Polymerization of Propylene Catalyzed by Ziegler-Natta Catalyst

Strong Influences of Cocatalyst on Ethylene/propylene Copolymerization with a MgCl2/SiO2/TiCl4/diester Type Ziegler–Natta Catalyst

Effect of Alkylaluminum Cocatalyst on Ethylene/1-Hexene Copolymerization and Active Center Distribution of MgCl2-supported Ziegler-Natta Catalyst

Effects of cocatalyst on ethylene-1-hexene copolymerization catalyzed by BCE catalyst

STUDIES ON COPOLYMERIZATION OF ETHYLENE-STYRENE WITH TITANIUM CATALYST COMPRISING RARE EARTH COMPOUND

Ethylene/1-Octadecene Copolymerization Using [Eta(5):Eta(1)-C5me4-4-R-1-6-R-C6h2o]Ticl2 Catalysts

Study on copolymerization of ethylene/1-hexene catalyzed by a novel polystyrene-supported metallocene catalyst

Study on Ethylene/1-Hexene Copolymerization Catalyzed by Α-Diimine Nickel Catalysts with Different Ligands

Effects of Alkylaluminum As Cocatalyst on the Active Center Distribution of 1-Hexene Polymerization with MgCl2-supported Ziegler–Natta Catalysts