Abstract:The impact of a titania (TiO2) support film surface on the catalytic activity of gold nanoparticles (Au NP) was investigated. Using the reactive dc-magnetron sputtering technique, TiO2 films with an amorphous, anatase, and nitrogen-doped anatase crystal structure were produced for a subsequent role as a support material for Au NP. Raman spectra of these TiO2 films revealed that both vacuum and NH3 annealing treatments promoted amorphous to anatase phase transformation through the presence of a peak in the 513-519 cm-1 spectral regime. Furthermore, annealing under NH3 flux had an associated blue shift and broadening of the Raman active mode at 1430 cm-1, characteristic of an increase in the oxygen vacancies (VO). For a 3 to 15 s sputter deposition time, the Au NP over TiO2 support films were in the 6.7-17.1 nm size range. From X-ray photoelectron spectroscope (XPS) analysis, the absence of any shift in the Au 4f core level peak implied that there was no change in the electronic properties of Au NP. On the other hand, spontaneous hydroxyl (-OH) group adsorption to anatase TiO2 support was instantly detected, the magnitude of which was found to be enhanced upon increasing the Au NP loading. Nitrogen-doped anatase TiO2 supporting Au NP with ~21.8 nm exhibited a greater extent of molecular oxygen adsorption. The adsorption of both -OH and O2 species is believed to take place at the perimeter sites of the Au NP interfacing with the TiO2 film. XPS analyses and discussions about the tentative roles of O2 and -OH adsorbent species toward Au/TiO2 systems corroborate very well with interpretations of density functional theory simulations.

Is Nanostructuring Sufficient To Get Catalytically Active Au?

Are Au Nanoparticles on Oxygen-Free Supports Catalytically Active?

Gold Catalysts Supported On Nanostructured Materials: Support Effects

X-ray Photoelectron Spectroscopy (XPS) Analysis of Ultrafine Au Nanoparticles Supported over Reactively Sputtered TiO2 Films

Atomic-Scale Observation of Bimetallic Au-CuOx Nanoparticles and Their Interfaces for Activation of CO Molecules.

Anchoring and Promotion Effects of Metal Oxides on Silica Supported Catalytic Gold Nanoparticles

Gold-Copper Nanoparticles: Nanostructural Evolution and Bifunctional Catalytic Sites

Ultrastable Au Nanocatalyst Supported on Surface-Modified TiO2 Nanocrystals

Stable mass-selected AuTiO x nanoparticles for CO oxidation

Atomic Layer Deposition of Gold Nanoparticles with Controlled Size and Distribution on Titania Support

The Dome of Gold Nanolized for Catalysis

Stable Mass-Selected AuTiOx Nanoparticles for CO Oxidation.

Catalytic Pt-on-Au Nanostructures: Why Pt Becomes More Active on Smaller Au Particles.

Quantitative Study of Au Catalytic Nanoparticles by Stem and Hrtem

Au/TiO2 Catalysts for CO Oxidation: Effect of Gold State to Reactivity

Structure–activity Relationships in Supported Au Catalysts

Yolk-Shell Gold Nanoparticles As Model Materials for Support-Effect Studies in Heterogeneous Catalysis: Au, @C and Au, @zro2 for Co Oxidation As an Example

Dynamic Atom Clusters on AuCu Nanoparticle Surface During CO Oxidation.

Nanoengineering Catalyst Supports Via Layer-by-layer Surface Functionalization

The State of Active Au Species in Au/Fe-O Catalyst During CO Catalytic Oxidation

Preparation of Monodisperse Au/Tio2 Nanocatalysts Via Self-Assembly