Improved Energy Storage Performance in Sandwiched Poly(vinylidene Fluoride)-Based Composites Assembling with In- Plane-Oriented BN Nanosheets and TiO2 Nanowires
Qian Wang,Hang Zhao,Lei Yin,Xiaoyu Ding,Xiuping Wei,Jinbo Bai
DOI: https://doi.org/10.1021/acsaem.2c03542
IF: 6.4
2022-01-01
ACS Applied Energy Materials
Abstract:With the rapid development of modern electronic and power systems, the low energy storage density is a critical weakness that greatly restricts the functional performance and application range of dielectric capacitors. Generally, the overall dielectric constant and breakdown strength are two key parameters that determine the energy storage density of a dielectric material. However, there is a significant negative coupling effect between these two parameters. Herein, a multilayer-structured composite showing an excellent energy storage performance was designed and fabricated by combining the continuous processes of spray-coating, melt mixing-extruding, in-situ dragging, alignment of oriented fibers, and hot-pressing procedures. This fabrication process has great potential in scaled production in industries. In this multilayered construction, the upper and lower layers are the PVDF thin layer deposited with in-plane oriented BN nanosheets (BNNSs), which provides a high breakdown strength for the composite. The intermediate layer is a PVDF-based composite uniformly dispersed with in-plane oriented TiO2 nanowires (TONWs), which enhance the interfacial and dipole polarizations in composites. The synergetic contribution of good dispersion and orientation perpendicular to the electric field minimizes the occurrence probability of ohmic contact and tunneling effects between TONWs, which limits the transport of charges in the intermediate polarized layer, increases the dielectric constant, and avoids the premature breakdown of composites. Under the extremely low filler loadings (BNNSs and TONWs are 0.11 and 1 wt % in the outer and middle layers, respectively), both the significantly enhanced excellent discharge energy density of 6.67 J/cm3 and breakdown strength of 376 MV/m were achieved from the BNNS/TONW/PVDF sandwich composite, which were 340 and 156% greater than those of the pure PVDF matrix (1.96 J/cm3 and 240 MV/m) respectively. This work provides an effective and feasible strategy for the enhancement of both energy storage density and scaled-production potential of polymer-based composite dielectrics.