Discharged Energy Density and Efficiency of Nanocomposites Based on Poly (vinylidene Fluoride) and Core-Shell Structured BaTiO3@Al2O3 Nanoparticles

Shaohui Liu,Jiao Wang,Haoshan Hao,Limin Zhao,Jiwei Zhai

DOI: https://doi.org/10.1016/j.ceramint.2018.09.077

IF: 5.532

2018-01-01

Ceramics International

Abstract:High discharged energy density and efficiency composites dielectric capacitors have gained world-wide attention. We apply a solution casting method to prepare films of PVDF nanocomposites containing sol-gel processed core-shell structured BaTiO3@Al2O3 nanoparticles. Their interfacial polarization and discharged energy density performance were investigated. On the morphological characterizations, the core-shell nanoparticles based on TEM were found to have Al2O3 with an average thickness of 6 nm, which acts as a shell layer coating on the surface of the BaTiO3-core. SEM results indicate that the core-shell nanoparticles created are dispersed uniformly in the PVDF matrix. Among the studied PVDF nanocomposites with different BaTiO3@Al2O3 nanoparticle loadings, the nanocomposite with 5 vol% BaTiO3@Al2O3 nanoparticles shows the highest discharged energy density of 6.1 J/cm(3), which is 1.2 times higher than that of the nanocomposite with pure BaTiO3 nanoparticles. For the 5 vol% of BaTiO3@Al2O3 nanoparticles added, the resulting nanocomposite exhibits a high efficiency of 81.6% below 1000 kV/cm and is higher than 66.5% at 2800 kV/cm. The enhanced discharged energy density and efficiency could be attributed to the improvement of the Maxwell-Wagner-Sillars interfacial polarization at the dynamic interface between PVDF matrix and BaTiO3@Al2O3 nanoparticles by which the difference of dielectric constant at the interface is reduced.