Effects of Si/B ratio on the isothermal crystallization behavior of FeNiSiBCuNb amorphous alloys
Zhe Chen,Qianke Zhu,Zhien Li,Qi Guo,Kewei Zhang,Yong Jiang
DOI: https://doi.org/10.1016/j.tca.2020.178854
IF: 3.5
2021-03-01
Thermochimica Acta
Abstract:<p>In the present work, (Fe<sub>40</sub>Ni<sub>40</sub>Si<em><sub>x</sub></em>B<em><sub>y</sub></em>Cu<sub>1</sub>)<sub>0.97</sub>Nb<sub>0.03</sub> (Si/B = 1:1, 1:2, and 1:3) alloys were prepared by the as-melt spun method. The effect of different Si/B ratios on the isothermal crystallization behavior of FeNiSiBCuNb glass alloys were investigated. The activation energies of the Si/B = 1:1, 1:2, and 1:3 alloys for nucleation and grain growth were calculated by the Kolmogorov-Johnson-Mehl-Avrami (KJMA) model as 123.6 kJ/mol and 207.3 kJ/mol, 151.0 kJ/mol and 251.3 kJ/mol, and 88.6 kJ/mol and 170.0 kJ/mol respectively; hence, crystal nuclei needed to cross a higher energy barrier in the growth process. The variation of local Avrami exponent <em>n</em>(<em>α</em>) with crystallization fraction <em>α</em> demonstrates that the crystallization mechanism was divided into three stages: <strong>i:</strong> initial crystallization stage with <em>n</em>>2, indicating that α-Fe(Si) phase or γ-(Fe, Ni)Si phase with a high nucleation rate stage, <strong>ii:</strong> middle crystallization stage with <em>n</em>≈2, indicating that FeNiB phase with a stable nucleation stage, and <strong>iii:</strong> the end of crystallization stage with <em>n</em><2, indicating that γ-(Fe, Ni)Si and FeNiB phases with a growth stage; The crystallization process was transformed from diffusion-controlled one-dimensional growth to diffusion-controlled three-dimensional growth.</p>
chemistry, physical, analytical,thermodynamics